国家自然科学基金项目;国家自然科学基金项目Reduction?magnetic separation of stainless steel pickling sludge by biomass
Yi ZHANG, Qiang SONG, Xinqian SHU*School of Chemistry and Environmental Engineering, China University of Mining and Technology (Beijing), Beijing 100083, China
Received:
2019-02-10Revised:
2019-03-29Online:
2019-12-22Published:
2019-12-22Contact:
Xinqian SHU 摘要/Abstract
摘要: 以生物质为还原剂,通过还原?磁选实验考察了还原温度、生物质种类和添加量、磁场强度及磁选粒度对回收酸洗污泥中铁的影响。结果表明,在反应温度为700℃、棉花秸秆添加量为5wt%、还原产物破碎至粒度小于0.074 mm颗粒占70%、磁场强度为200 mT条件下磁选回收,所得产物中铁品位为67.72wt%、回收率达91.83%。
引用本文
张祎 宋强 舒新前. 生物质还原-磁选不锈钢酸洗污泥[J]. 过程工程学报, 2019, 19(6): 1111-1119.
Yi ZHANG Qiang SONG Xinqian SHU. Reduction?magnetic separation of stainless steel pickling sludge by biomass[J]. Chin. J. Process Eng., 2019, 19(6): 1111-1119.
使用本文
导出引用管理器 EndNote|Ris|BibTeX
链接本文:http://www.jproeng.com/CN/10.12034/j.issn.1009-606X.219134
http://www.jproeng.com/CN/Y2019/V19/I6/1111
参考文献
[1]房金乐,杨文涛.不锈钢酸洗污泥的处理现状及展望[J].中国资源综合利用, 2014, 32(11):24-28 [2]Junxue Z, Zhongyu Z, Ruimeng S, et al.Issues Relevant to Recycling of Stainless-Steel Pickling Sludge [J].JOM, 2018 [3]Masahiko Ito, Rinso Tachibana, Katsuji Fukushima, .Characteristics and Production Mechanism of Sulfuric Acid and Nitric-Hydrofluoric Acid Pickling Sludge Produced in Manufacture of Stainless Steel[J].Journal of Chemical Engineering Of Japan, 1998, , Vol.31 (4):589-595 [4]G.Ma,AM. Garbers-Craig Cr(VI) containing electric furnace dusts and filter cake from a stainless steel waste treatment plant: Part 1 – Characteristics and microstructure[J].Ironmaking & Steelmaking, 2006, Vol.33(3):229-237 [5]Ma P, Lindblom B, Bo Bj?rkman.Experimental studies on solid﹕tate reduction of pickling sludge generated in the stainless steel production[J].Scandinavian Journal of Metallurgy, 2005, 34(1):31-40 [6]Potesser M,Schnideritsch H.Chromium in different meta Vurgical residues with special regard to hexavalent chromium. EMC uropean Metallurgical Conference) Proceeding [J].Dresden, Germany, 2005, (3: 1205.) [7]朱立,孙本良.钢材酸洗技术 [M]. 北京:化学工业出版社,2007. [8]柳雨.不锈钢企业含重金属污泥的无害化资源化处理技术研究[J].中国废钢铁, 2007, 23(1):- [9]刘平阳,谈定生,丁伟中.不锈钢酸洗污泥中重金属的浸出试验研究[J].有色金属材料与工程, 2017, 38(03):149-153 [10]Zhang L, Liu Y S.A novel method for harmless disposal and resource reutilization of steel wire rope sludges[J].Environ Sci Pollut Res Int, 2016, 23(19):19797-19805 [11]张景,孙映,刘旭隆,等.还原-磁选不锈钢酸洗污泥中的金属[J].过程工程学报, 2014, 14(05):782-786 [12]Ma P, Lindblom B, Bjorkman B.Experimental Studies on Solid-state Reduction of Pickling Sludge Generated in the Stainless Steel Production[J].Scand. J. Metall., 2005, 34(1):31- [13]徐科.钢铁厂废水污泥中铬的回收研究 [D]. 上海:同济大学,2006. I-2 [14]张士元,冯雅丽,李浩然.生物质磁化焙烧赤铁矿的研究[J].矿业工程, 2016, 14(04):31-33 [15]李恒,刘晓明,赵喜彬,等.生物质松木锯末中低温还原高铁拜耳法赤泥[J].北京科技大学学报, 2017, 39(9):1331-1338 [16]Demirbes A, Arin G.An overview of biomass pyrolysis[J].Energy Sources, 2002,, 24(5):471-482 [17]黄希祜.钢铁冶金原理 [M]. 北京:冶金工业出版社, 2002. 285. [18]龚俊.从含铁尘泥回收铁的试验研究 [D]. 内蒙古科技大学, 2010. [19]王艺慈,罗果萍,柏京,等.F、K、Na对烧结固相反应影响的研究[J].钢铁, 2008, (07):12-15 [20]Kamijo C,Hoshi M,Kawaguchi T,et al.Production of direct reduced iron by a sheet material inserting metallization method[J].ISIJ International, 2001, 41(sup):13-16 [21]Andres J M, Narros A, Rodriguez M E.Air-steam gasification of sewage sludge in a bubbling bed reactor: Effect of alumina as a primary catalyst[J].Fuel Processing Technology, 2011, 92(3):433-440 [22]张秀梅,陈冠益,孟祥梅,等.催化热解生物质制取富氢气体的研究[J].燃料化学学报, 2004, 32(4):446-449 [23]Yang H P, Yan R, Chen H P, et al..In-depth investigation of biomas pyrolysis based on three major components:hemicellulose,cellulose and lignin[J].Energy Fuels, 2006, 20(1):388-393 [24]陈应泉,王贤华,李开志,等.温度对棉杆热解多联产过程中产物特性的影响[J].中国电机工程学报, 2012, 32(17):117-124 [25]梁雪海.论矿石粒度对弱磁选的影响[J].河北冶金, 1990, (5):1-4 [26]春铁军,吴雪,宁超,等.菱铁矿磁化焙烧与磁选分离制备铁精矿 [J].过程工程学报, 2016, 16(2):233-237 |
相关文章 15
[1] | 王耀宁 马红周 王致娴 王丁丁 王碧侠. 铝与硅铁混合物还原煅烧白云石中氧化镁[J]. 过程工程学报, 2021, 21(4): 440-445. |
[2] | 王启立 张锋涛 高晓峰 胡建文. 多晶硅生产用煤基高纯石墨性能及应用[J]. 过程工程学报, 2021, 21(3): 323-331. |
[3] | 周玥 郭晓晶 李宣江 高璐 洪枫 乔锦丽. 不同浸渍时间对CuO/Cu@BC电极催化CO2还原性能的影响[J]. 过程工程学报, 2020, 20(8): 989-996. |
[4] | 金化成 白柳杨 范俊梅 侯果林 丁 飞 袁方利. 高频氢等离子体增强还原制备超细铜粉[J]. 过程工程学报, 2020, 20(8): 979-988. |
[5] | 李小明 闻震宇 李怡 王伟安 邢相栋. 碳酸钠对镍渣碳热还原的催化作用[J]. 过程工程学报, 2020, 20(2): 182-188. |
[6] | 张晶晶 李建 肖清贵 张绘 杜嬛 薛天艳 齐涛. 纳米Co/rGO磁性复合吸附材料的制备及对Cu2+的吸附性能[J]. 过程工程学报, 2020, 20(12): 1472-1482. |
[7] | 徐霞 吴云 赵勇 李宏强 彭敏 徐建. 微波烘焙预处理降解玉米秸秆[J]. 过程工程学报, 2019, 19(S1): 109-114. |
[8] | 杨时颖 郑经纬 李宝霞. 生物质制甲醇系统CO2捕集过程的设计模拟及技术经济性分析[J]. 过程工程学报, 2019, 19(6): 1250-1256. |
[9] | 吴名涛 邵大伟 郭强 李永利 齐涛. 不锈钢酸洗废水钙钠中和沉淀与碳热还原协同处理新工艺[J]. 过程工程学报, 2019, 19(5): 989-996. |
[10] | 戴广平 石瑀 周世伟 李博 魏永刚. 铜熔渣喷吹地沟油还原贫化[J]. 过程工程学报, 2019, 19(4): 759-766. |
[11] | 王金德 裴海鹏 金保昇 戴昕 孙漪清. 高铝矾土改性对稻草热解与气化特性的影响[J]. 过程工程学报, 2019, 19(4): 783-791. |
[12] | 孙海韵 马培勇 邢勇强 邢献军 陈明明. 基于SLMD预测生物质三组分混合成型特性[J]. 过程工程学报, 2019, 19(3): 575-580. |
[13] | 尤晶 王耀武. 皮江法炼镁还原机理[J]. 过程工程学报, 2019, 19(3): 560-566. |
[14] | 朱小芳 李庆 张盈 房志刚 郑诗礼 孙沛 夏阳. 热化学还原法制备金属钛的技术研究进展[J]. 过程工程学报, 2019, 19(3): 456-464. |
[15] | 孔玮佳 于守泉 戈敏 张伟刚 杜令忠. 碳化锆陶瓷有机前驱体的热解过程[J]. 过程工程学报, 2019, 19(3): 623-630. |
PDF全文下载地址:
http://www.jproeng.com/CN/article/downloadArticleFile.do?attachType=PDF&id=3347