西安建筑科技大学冶金工程学院，陕西 西安 710055
收稿日期:2019-04-25修回日期:2019-06-18出版日期:2020-02-22发布日期:2020-02-19通讯作者:邢相栋基金资助:中国国家自然科学基金;中国国家自然科学基金Catalytic effect of sodium carbonate on the carbothermic reduction of nickel slag
Xiaoming LI, Zhenyu WEN, Yi LI, Weian WANG, Xiangdong XING*School of Metallurgical Engineering, Xi?an University of Architecture and Technology, Xi?an, Shaanxi 710055, China
Received:2019-04-25Revised:2019-06-18Online:2020-02-22Published:2020-02-19摘要/Abstract
摘要： 以全铁含量39.40wt%和SiO2含量32.50wt%的镍渣为原料，针对其中的铁以铁橄榄石形式存在难以直接还原磁选提铁的问题，在镍渣中添加不同质量比的碳酸钠促进镍渣碳热还原，进行了热力学计算和实验验证。结果表明，碳酸钠添加量由0增加至6wt%时，还原产物中铁的金属化率和回收率不断增大，继续增大碳酸钠添加量至8wt%时，铁的金属化率和回收率略有减小。不添加碳酸钠的还原产物中铁粒径很小，平均粒径为6 ?m，难还原的铁橄榄石大量存在，而加入6wt%碳酸钠的还原产物中铁粒径粗大，平均粒径增大至17 ?m，铁橄榄石含量明显降低，金属铁的XRD衍射峰强度明显增加。
引用本文
李小明 闻震宇 李怡 王伟安 邢相栋. 碳酸钠对镍渣碳热还原的催化作用[J]. 过程工程学报, 2020, 20(2): 182-188.
Xiaoming LI Zhenyu WEN Yi LI Weian WANG Xiangdong XING. Catalytic effect of sodium carbonate on the carbothermic reduction of nickel slag[J]. Chin. J. Process Eng., 2020, 20(2): 182-188.
使用本文
导出引用管理器 EndNote|Ris|BibTeX
链接本文:http://www.jproeng.com/CN/10.12034/j.issn.1009-606X.219187
http://www.jproeng.com/CN/Y2020/V20/I2/182
参考文献
| [1]张振强，崔雅茹，赵俊学，等.镍火法熔炼高钙低硅渣提取铁的研究[J].钢铁研究学报, 2013, 25(07):23-26 [2]矿产资源工业要求手册编委会.矿产资源工业要求手册 (2012年修订版) [M]. 地质出版社, 2012: 17. [3]Piatak N M, Parsons M B, Ii R R S.Characteristics and environmental aspects of slag: A review [J].Applied Geochemistry, 2014, 57(1):236-266 [4]Oh C J, Lee S O, Yang H S, et al.Selective leaching of valuable metals from waste printed circuit boards[J].Air Repair, 2003, 53(7):897-902 [5]Zhu D Q, Zhou X L, Luo Y H, et al.Reduction smelting low ferronickel from pre-concentrated nickel-iron ore of nickel laterite[J].High Temperature Materials & Processes, 2016, 35(10):1031-1036 [6]You Z X, Li G H, Wen P D, et al.Reduction of Sn-bearing iron concentrate with mixed H2CO gas for preparation of Sn-enriched direct reduced iron[J].Metallurgical and Materials Transactions B, 2017, 48(3):1486-1493 [7]陈伟鹏, 李光卫, 赵增武, 等.高铁煤泥作还原剂直接还原褐铁矿研究[J].矿冶工程, 2017, 37(01):68-72 [8]庞建明，郭培民，赵沛.铜渣低温还原与晶粒长大新技术 [J].有色金属(冶炼部分), 2013, 1(3):51-53-57 [9]赵志龙，唐惠庆，郭占成.气氛下、对金属铁析出微观形貌的影响[J].矿冶工程, 2012, 32(05):105-109 [10]Jiang T, Liu M D, Li G H, et al.Effects of sodium-salt on Al-Fe separation by reduction roasting for high-aluminum content limonite[J].Chinese Journal of Nonferrous Metals, 2010, 20(6):1226-1233 [11]鲁逢霖，郭玉华，张颖异, 等.镍渣直接还原磁选提铁试验[J].钢铁, 2014, 49(02):19-23 [12]Bai S J, Wen S M, Liu D W, et al.Beneficiation of high phosphorus limonite ore by sodium-carbonate-added carbothermic reduction[J].Isij International, 2012, 52(10):1757-1763 [13]Bai S J, Wen S M, Liu D W, et al.Catalyzing carbothermic reduction of siderite ore with high content of phosphorus by adding sodium carbonate[J].Isij International, 2011, 51(10):1601-1607 [14]丁闪，薛庆国，佘雪峰，等.碳酸钙对钒钛磁铁精矿直接还原-熔分的影响[J].钢铁, 2014, 49(8):15-20 [15]Basumallick A.Influence of CaO and Na2CO3 as additive on the reduction of hematite-lignite mixed pellets[J].Transactions of the Iron & Steel Institute of Japan, 2007, 35(9):1050-1053 [16]曹羽鑫，王恒辉，马江华，等.添加剂对铁精矿制备还原铁粉的影响[J].过程工程学报, 2018, 18(01):133-139 [17]Wang X D, Qu R T, Wu S J, et al.Notch fatigue behavior: metallic glass versus ultra-high strength steel[J].Scientific Reports, 2016, 6(1):355-357 [18]An X W, Wang J S, She X F, Ding Y G, et al.New technologies of energy saving and low CO2 emission for iron making [J]. Advanced Materials Research, 2012, 463-464: 957-961.[J].Advanced Materials Research, 2012, 463-464(1):957-961 |
相关文章 15
| [1] | 吴名涛 邵大伟 郭强 李永利 齐涛. 不锈钢酸洗废水钙钠中和沉淀与碳热还原协同处理新工艺[J]. 过程工程学报, 2019, 19(5): 989-996. |
| [2] | 孔玮佳 于守泉 戈敏 张伟刚 杜令忠. 碳化锆陶瓷有机前驱体的热解过程[J]. 过程工程学报, 2019, 19(3): 623-630. |
| [3] | 王凯飞 张国华 王璐 周国治. 添加Fe2O3对碳热还原含钛高炉渣的影响[J]. 过程工程学报, 2018, 18(6): 1276-1282. |
| [4] | 何延波 吴照金 高志芳 岳海峰 刘伟明 王平. 钢渣有价组分的分部高附加值利用[J]. 过程工程学报, 2017, 17(5): 1028-1034. |
| [5] | 李国洲 申莹莹 马泳波 张燕云 陈敏 杜雪岩. 碱度对熔融改质镍渣中磁铁矿相析出长大的影响[J]. 过程工程学报, 2017, 17(4): 791-796. |
| [6] | 王安仁 袁吉峰. 氮化钒制备热力学和动力学[J]. 过程工程学报, 2017, 17(3): 558-564. |
| [7] | 刘能生彭金辉张利波蔺琎. 高铝粉煤灰碳酸钠焙烧与酸浸提铝的动力学[J]. 过程工程学报, 2016, 16(2): 216-221. |
| [8] | 田勇攀潘晓林于海燕涂赣峰. Na4Ca3(AlO2)10的合成和浸出行为[J]. 过程工程学报, 2016, 16(2): 228-232. |
| [9] | 李慧龙萍任新林陈秀敏杨斌. 复杂锡精矿还原熔炼过程中元素在金属和渣相中的分布[J]. 过程工程学报, 2016, 16(1): 132-137. |
| [10] | 余国林张盈郑诗礼邹兴王晓辉张懿. 含砷钴镍渣中砷碱介质氧化浸出机理[J]. , 2013, 13(6): 939-945. |
| [11] | 杨勇李解李保卫张邦文韩继铖. 铌酸铁碳热还原的等温动力学分析[J]. , 2013, 13(3): 430-435. |
| [12] | 高明磊陈东辉石立新李兰杰周冰晶祁健. 碳酸钠焙烧铝系钒铁炉渣共提取钒与铝[J]. , 2012, 12(4): 576-582. |
| [13] | 郭强曲景奎韩冰冰魏广叶齐涛. 碳酸钠碱熔处理褐铁型红土镍矿的热力学分析与实验研究[J]. , 2011, 11(1): 72-78. |
| [14] | 张卫嘉郑诗礼邹兴张盈张懿. 杂质对甲醇分解铝酸钠溶液制备氢氧化铝的影响[J]. , 2010, 10(5): 921-926. |
| [15] | 熊利芝陈启元尹周澜张平民. 真空碳热还原氧化锌矿动力学[J]. , 2010, 10(1): 133-137. |
PDF全文下载地址:
http://www.jproeng.com/CN/article/downloadArticleFile.do?attachType=PDF&id=3396