Subcritical hydrothermal heterogeneous oxidation of semi-dry desulfurization ash from iron ore sintering flue gas

Rufei WEI¹, Longzhi CHEN³, Hongming LONG^1,2*, Yifan WANG¹, Jiaxin LI¹, Yafei LI¹, Ming XUAN²

1. School of Metallurgical Engineering, Anhui University of Technology, Ma?anshan, Anhui 243032, China 2. Key Laboratory of Metallurgical Emission Reduction & Resources Recycling (Anhui University of Technology), Ministry of Education, Ma?anshan, Anhui 243032, China3. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China

Received:2018-09-28Revised:2018-11-16Online:2019-06-22Published:2019-06-20
Contact:LI Jia-xin

摘要/Abstract

摘要： 采用亚临界水热氧化法对铁矿烧结烟气半干法脱硫灰进行氧化，采用单因素变量法考察初始压强、温度、固液比、反应时间对脱硫灰中CaSO3氧化的影响。结果表明，适当增加初始压强、提高氧化温度、降低固液比及增加氧化时间可有效改善脱硫灰中CaSO3的氧化效果，温度对CaSO3氧化影响最显著。在初始压强4 MPa、反应温度240℃、反应时间120 min、固液质量比为1:30的条件下，脱硫灰中CaSO4定向析出，呈纤维状，为脱硫灰水热氧化同步合成CaSO4晶须提供了可能。

引用本文

魏汝飞陈龙智龙红明王毅璠李家新李亚飞宣明. 铁矿烧结烟气半干法脱硫灰亚临界水热非均相氧化[J]. 过程工程学报, 2019, 19(3): 603-608.
Rufei WEI Longzhi CHEN Hongming LONG Yifan WANG Jiaxin LI Yafei LI Ming XUAN. Subcritical hydrothermal heterogeneous oxidation of semi-dry desulfurization ash from iron ore sintering flue gas[J]. Chin. J. Process Eng., 2019, 19(3): 603-608.

使用本文

0
/ / 推荐
导出引用管理器 EndNote|Ris|BibTeX
链接本文:http://www.jproeng.com/CN/10.12034/j.issn.1009-606X.218291
http://www.jproeng.com/CN/Y2019/V19/I3/603

参考文献

[1] 刘征建，张建良，杨天钧．烧结烟气脱硫技术的研究与发展[J]．中国冶金，2009．
Liu Zhengjian, Zhang Jianliang, Yang Tianjun. Research and development of sintering flue gas desulphurization technology[J]. China Metallurgy, 2009, 19( 2) : 1-5( in Chinese).
[2] 贺亮，张少峰．半干法烟气脱硫技术研究现状及进展[J]．天津化工，2007(02)：18-20．
He Liang, Zhang Shaofeng. Research Status and Development of Semi-dry Flue Gas Desulfurization Technology[J]. Tianjin Chemical, 2007 (02) : 18-20( in Chinese).
[3] 陈袁魁，包正宇，龙世宗，等．高钙脱硫灰渣用作水泥原料的研究[J]．水泥工程，2006(04)：10-12．
Chen Yuankui, Bao Zhengyu, Long Shizong, et al. Study on high calcium desulfurization ash used as cement raw material[J]. Cement engineering, 2006 (04) : 10-12( in Chinese).
[4] 杨亚欣，马玉香，任爱玲，等．烧结烟气脱硫技术及脱硫产物综合利用研究进展[J]．环境科学导刊，2009(06)：67-70．
Yang Yaxin, Ma Yuxiang, Rrn Ailng, et al. Research progress on sintering flue gas desulfurization technology and comprehensive utilization of desulfurization products[J]. Environmental Science Guide, 2009 (06) : 67-70( in Chinese).
[5] 林贤熊，叶光锐．排烟脱硫副产品亚硫酸钙作水泥缓凝剂的研究[J]．粉煤灰，2003(02)：15-17．
Lin Xianxiong, Ye Guangrei. Study on calcium sulfite as a cement retarder for by-product of flue gas desulfurization[J]. Fly ash, 2003 (02) : 15-17( in Chinese).
[6] 徐胜光，李淑仪，蓝佩玲，等．燃煤烟气脱硫副产物对花生作物营养效应及其机理[J]．生态环境，2003(04)：415-418．
Xu Shengguang, Li Shuyi, Lan Peiling, et al. Nutritional Effects and Mechanism of By-products from Coal-fired Flue Gas Desulfurization on Peanut Crops[J]. ecosystem,2003 (04) : 415-418( in Chinese)
[7] 柯亮，石林，耿曼．脱硫灰渣与钾长石混合焙烧制钾复合肥的研究[J]．化工矿物与加工，2007(07)：17-20．
Ke Liang, Shi Lin, Geng Man. Study on the Preparation of Potassium Compound Fertilizer by Desulfurization Ash and Potash Feldspar[J]. Chemical minerals and processing, 2007 (07) : 17-20( in Chinese).
[8] Lancia A, Musmarra D, Pepe F. Uncatalyzed heterogeneous oxidation of calcium bisulfite[J]. Chemical Engineering Science, 1996,16(51):3889-3896.
[9] Ahmed M G, Anurag G. Characterization of the Product of the Thiosulfate Process for Desulfurization of Flue Gases[J]. Ind. Eng. Chem. Res., 1994(33):1145-1149.
[10] Li Y, Sadakata M. Study of gypsum formation for appropriate dry desulfurization process of flue gas[J]. Fuel, 1999,78(9):1089-1095.
[11] 杨剑，文娟，董凌燕，等．烟气脱硫过程锰催化氧化亚硫酸钙的研究[J]．环境工程学报，2007(09)：109-112．
Yang Jian, Wen Juan, Dong Lingyan, et al. Manganese Catalytic Oxidation of Calcium Sulfite in Flue Gas Desulfurization Process[J]. Journal of Environmental Engineering, 2007 (09) : 109-112( in Chinese).
[12] 姚璐，刘清才，方诗惠，等．半干法烧结烟气脱硫灰的氧化改性[J]．环境工程学报，2016(06)：3147-3151．
Yao Lu, Liu Qingcai, Fang Shihui, et al. Oxidation modification of semi-dry sintering flue gas desulfurization ash[J]. Journal of Environmental Engineering, 2016 (06) : 3147-3151( in Chinese).
[13] 杨新亚，张丽英，刘洪波．干法与半干法脱硫渣中亚硫酸钙的低温催化氧化的研究[J]．粉煤灰，2006(04)：10-12．
Yang Xinya, Zhang Liying, Liu Hongbo. Study on Low Temperature Catalytic Oxidation of Calcium Sulfite in Dry and Semi-dry

相关文章 15

[1]	王成彦曹志河马保中陈永强. 红土镍矿硝酸加压浸出工艺[J]. 过程工程学报, 2019, 19(S1): 51-57.
[2]	张娜钟莉段东平. 油酸辅助水热合成纳米钛酸锶的性能调控与表征[J]. 过程工程学报, 2019, 19(6): 1212-1219.
[3]	李崇周俊刘瑶周志茂. 我国废硫酸产生及综合利用现状[J]. 过程工程学报, 2018, 18(S1): 24-34.
[4]	刘悦曹磊李达曹坤隋富生赵伟吕伟齐涛. 混合表面活性剂体系合成锆掺杂介孔分子筛[J]. 过程工程学报, 2018, 18(5): 1082-1087.
[5]	李艳萍闫东伟周少雄. 锰钴复合氧化物MnCo2O4磁性纳米晶的制备及表征[J]. 过程工程学报, 2017, 17(6): 1287-1290.
[6]	何延波吴照金高志芳岳海峰刘伟明王平. 钢渣有价组分的分部高附加值利用[J]. 过程工程学报, 2017, 17(5): 1028-1034.
[7]	李磊廖彬王华胡建杭邱在军桑秀丽. 锡铁矿硫化焙烧脱锡[J]. , 2013, 13(3): 409-414.
[8]	周晶晶刘开宇孔春龙陈亮. 金属有机骨架材料MIL-101(Cr)-NH2的合成及其气体吸附性能[J]. , 2013, 13(1): 146-151.
[9]	赵凯程相利齐渊洪甄常亮师学峰. 水淬铜渣的矿物学特征及其铁硅分离[J]. , 2012, 12(1): 38-43.
[10]	李云伟朱永平. 针状海绵态铁粉的研制及其在热电池中的应用[J]. , 2011, 11(5): 875-879.
[11]	许海艇徐光青郑治祥吴玉程. 不同硅源对水热合成Zn2SiO4:Mn荧光材料形貌及性能的影响[J]. , 2011, 11(3): 509-513.
[12]	余德麒施正伦肖文丁李戈跃骆仲泱岑可法. 石煤灰渣二次焙烧稀酸浸出提钒工艺条件[J]. , 2010, 10(4): 673-678.
[13]	孙淑英张钦辉于建国. 尖晶石型LiMn2O4的水热合成及其锂吸附性能[J]. , 2010, 10(1): 185-189.
[14]	刘艳辉薛向欣宋海. 油页岩渣制备沸石及其吸附Cr6+性能[J]. , 2008, 8(6): 1108-1111.
[15]	孙维国杨建华王爱芳王金渠韩会林鲁金明. 两步变温水热合成制备纯硅分子筛膜及其渗透性能[J]. , 2008, 8(3): 599-602.

PDF全文下载地址:

http://www.jproeng.com/CN/article/downloadArticleFile.do?attachType=PDF&id=3278