国家重点研发计划Effect of ρ-Al2O3 addition on the properties of in situ reaction-bonded porous SiC membrane support
Zhiyong LUO1, Kaiqi LIU2*, Wei HAN1, Wenqing AO1, Yunfa CHEN21. Beijing Key Laboratory of Advanced Ceramic and Refractories, Central Iron & Steel Research Institute, Beijing 100081, China 2. State Key Laboratory of Multi-phase Complex Systems, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, China
Received:
2018-05-28Revised:
2018-08-07Online:
2019-04-22Published:
2019-04-18Supported by:
National Key R&D Program of China摘要/Abstract
摘要: 以黑色碳化硅为骨料,添加不同含量的ρ-Al2O3,在1430℃、无压条件下,用碳化硅表面氧化产生的SiO2与Al2O3反应制备多孔碳化硅膜支撑体,研究了ρ-Al2O3添加量对碳化硅支撑体粘结相组成及性能的影响。结果表明,ρ-Al2O3添加量由3wt%增加到15wt%时,试样烧结后粘结相中莫来石相增多,石英相减少但不能完全消除,支撑体的显气孔率降低,孔径减小,透气度由1127.8 m3?cm/(m2?h?kPa)下降到210.4 m3?cm/(m2?h?kPa);支撑体抗弯强度先增大后降低,ρ-Al2O3添加量为9wt%时,支撑体抗弯强度为25.1 MPa,透气度为372.7 m3?cm/(m2?h?kPa),支撑体的综合性能满足高温含尘气体过滤的要求。
引用本文
罗志勇 刘开琪 韩伟 敖雯青 陈运法. ρ-Al2O3添加量对原位反应结合碳化硅膜支撑体性能的影响[J]. 过程工程学报, 2019, 19(2): 407-412.
Zhiyong LUO Kaiqi LIU Wei HAN Wenqing AO Yunfa CHEN. Effect of ρ-Al2O3 addition on the properties of in situ reaction-bonded porous SiC membrane support[J]. Chin. J. Process Eng., 2019, 19(2): 407-412.
使用本文
导出引用管理器 EndNote|Ris|BibTeX
链接本文:http://www.jproeng.com/CN/10.12034/j.issn.1009-606X.218225
http://www.jproeng.com/CN/Y2019/V19/I2/407
参考文献
[1] 薛友祥, 孟宪谦, 李宪景, 等.热气体净化用的高温陶瓷过滤材料[J].现代技术陶瓷, 2005, 27(3):18-25 [2]Alvin MA.Advanced ceramic materials for use in high-temperature particulate removal systems[J].Ind. Eng. Chem. Res., 1996, 35(10):3384-98 [3]G.Agnieszka,SLudoslaw,L. Pawel.Microstructure and mechanical properties of silicon carbide pressureless sintered with oxide additives[J].J. Eur. Ceram. Soc., 2007, 27(2-3):781-789 [4]S.Ding,SZhu,et al. Fabrication of mullite-bonded porous silicon carbide ceramics by in situ reaction bonding[J].J. Eur. Ceram. Soc., 2007, 2007,27(4):2095-2102 [5]S.Zhu,SDing,H.Xi,Q.Li,et al. Preparation and characterization of SiCcordierite composite porous ceramics[J].Ceram. Int., 2007, 33(1):115-118 [6]Y.S. Chun and YW. Kim. Processing and mechanical properties of porous silica-bonded silicon carbide ceramics[J].Met. Mater. Int., 2005, 11(5):351-355 [7]S.H. Chae,YW. Kim,I.H. Song,et al. Low Temperature Processing and Properties of Porous Frit-Bonded SiC Ceramics[J].J. Korean Ceram. Soc., 2009, 46(5):488-492 [8] Ding SQ, Zhu S, Zeng YP, Jiang DL.Effect of Y2O3 addition on the properties of reaction-bonded porous SiC ceramics[J].Ceram. Int., 2006, 32(4):461-466 [9]J.H.Eom,YW. Kim,S. Raju. Processing and properties of macroporous silicon carbide ceramics: A review[J].J. Asian Ceram. Soc., 2013, 1(4):220-242 [10]A.Dey,NKayal and O. Chakrabarti. Preparation of mullite bonded porous SiC ceramics by an infiltration method[J].J. Mater. Sci., 2011, 46(16):5432-5438 [11]B.V.M. Kumar,JH. Eom,Y.W. Kim,I.H. Song and H.D. Kim.Effect of aluminum hydroxide content on porosity and strength of porous mullite-bonded silicon carbide ceramics[J].J. Ceram. Soc. Jpn., 2011, 119(1389):367-370 [12]B.V.M. Kumar,JH. Eom,Y.W. Kim,I.S. Han and S.K. Woo,Effect of aluminum source on flexural strength of mullite-bonded porous silicon carbide ceramics[J].J. Ceram. Soc. Jpn., 2010, 118(1373):13-18 [13]Alvin M A.Assessment of ceramic and metal media filters in advanced power systems. Proceedings of ASME Turbo Expo 2001. June 4-7, 2001, New Orieans, LA, USA. [14]罗志勇, 刘开琪, 韩伟, 等.不同含铝微粉对原位反应结合SiC多孔陶瓷膜支撑体性能的影响[J]. 耐火材料, 2018, 52(5)(已收录). [15]Toshihiro Isobe, Yoshikazu Kameshima, Akira Nakajima, et al.Gas permeability and mechanical properties of porous alumina ceramics with unidirectionally aligned pores[J].J. Eur. Ceram. Soc., 2007, 27(1):53-59 [16] 周谟仁.流体力学泵与风机[M]. 中国建筑工业出版社, 1979: 51, 88-124. |
相关文章 1
[1] | 张国军. 纳米复相结构陶瓷的原位反应合成[J]. , 2002, 2(4): 0-0. |
PDF全文下载地址:
http://www.jproeng.com/CN/article/downloadArticleFile.do?attachType=PDF&id=3247