Controlling cadmium pollution with fly ash-bentonite cut-off wall

HUANG Qinqin^1,2,,
LIU Guo^1,2,,
WEN Meiyan^1,2,
YE Changwen^1,2,
LIU Yanhui^1,2,
ZENG Yi^1,2
1.State Key Laboratory of Geohazard Prevention and Geoenvironment Protection, Chengdu University of Technology, Chengdu 610059, China
2.State Environmental Protection Key Laboratory of Synergetic Control and Joint Remediation for Soil & Water Pollution, Chengdu University of Technology, Chengdu 610059, China

-->

摘要
HTML全文
图(0)表(0)
参考文献(36)
相关文章
施引文献
资源附件(0)
访问统计

摘要:为了探究以固体废弃物粉煤灰和吸附性强的膨润土为材料制备的阻隔墙对镉污染的控制效果，采用微观表征、渗透实验、吸附实验、穿透实验、单轴抗压实验和侵蚀实验研究阻隔墙的性能。结果表明：阻隔墙材料的最佳质量配比为粉煤灰∶膨润土=5∶1，水泥质量占整个体系的5%；所得阻隔墙的渗透系数为1.11×10-8 m·s-1；最大抗压强度291.97 kPa；复合材料最大吸附率为98.38%。同时发现，固化体系中膨润土填充在粉煤灰球体的空隙处和表面，粉煤灰和膨润土都与水泥产生了水化产物和胶结物，Cd2+附着在阻隔材料表面；阻隔墙吸附的系统符合准一级动力学模型和Freundlich方程；系统的总吸附速率受液膜扩散与颗粒扩散同时影响；阻隔墙对Cd2+作用以物理吸附为主；墙体的抗碱腐蚀性比抗酸腐蚀性、耐有机污染物腐蚀性强。该研究可为将阻隔墙技术应用于地下水污染场地提供理论依据。
关键词: 镉污染防治/
阻隔墙/
粉煤灰资源化/
改性增强膨润土/
重金属物理吸附

Abstract:In this study, microscopic characterization, permeation and adsorption experiments, as well as penetration, uniaxial compressive and erosion experiments were conducted to investigate the performance of a cut-off wall on cadmium pollution control, which was made of a kind of solid waste-fly ash and bentonite with high absorbing capacity. The results showed that the optimum mass ratio of fly ash to bentonite in a cut-off wall is 5 to 1, and the cement accounts for 5% of the cut-off wall mass. Its permeability and the maximum compression strength are 1.11×10-8m·s-1 and 291.97 kPa, respectively. The maximum Cd adsorption efficiency of the composite material is 98.38%. The microscopic observation indicated that the interstices and surface of the fly ash spheres were filled by bentonite in the curing system. Both fly ash and bentonite reacted with cement, and hydration products and agglutinates formed, then Cd2+ adhered to the surface of barrier material. The Cd adsorption process on the cut-off wall fitted the quasi-first-order dynamic model and Freundlich equation, which indicated that the total adsorption rate was controlled by both liquid film and intra-particle diffusions. The Cd2+ adsorption on the cut-off wall is mainly considered as a physical process. The alkali corrosion resistance of the cut-off wall is stronger than its acid corrosion resistance and organic pollutant corrosion resistance. The results implied that the cut-off wall could be used to reclaim the groundwater contaminated sites.
Key words:cadmium pollution prevention/
cut-off wall/
fly ash recycling/
modified and enhanced bentonite/
physical adsorption of heavy metals.

[1]	SKIBIN G M, CHIZH I N. Evaluation of cutoff walls influence on stresses distribution under adjacent foundations[J]. Procedia Engineering, 2016, 150: 2261-2265.
[2]	吕淑清. 土壤-膨润土泥浆墙对污染物的阻截性能及机理研究[D]. 长春: 吉林大学, 2015.
[3]	XU H, ZHU W, QIAN X, et al. Studies on hydraulic conductivity and compressibility of backfills for soil-bentonite cutoff walls[J]. Applied Clay Science, 2016, 132-133: 326-335.
[4]	万勇, 薛强, 赵立业, 等. 干湿循环对填埋场压实黏土盖层渗透系数影响研究[J]. 岩土力学, 2015, 37(3): 679-686.
[5]	唐兴萍, 周雄, 张金洋, 等. TiO2/膨润土复合材料对Hg2+的吸附性能研究[J]. 环境科学, 2017, 38(2): 608-615.
[6]	WANG Y, CHEN Y, XIE H, et al. Lead adsorption and transport in loess-amended soil-bentonite cut-off wall[J]. Engineering Geology, 2016, 215: 69-80.
[7]	周春宇. 粉煤灰、硅灰制备有序介孔材料及其有机染料去除性能研究[D]. 北京: 中国地质大学(北京), 2017.
[8]	杜延军, 范日东. 改性土-膨润土竖向隔离墙材料的压缩及渗透特性实验研究[J]. 岩土力学, 2011, 37(S1): 49-54.
[9]	TAKAI A, INUI T, KATSUMI T. Evaluating the hydraulic barrier performance of soil-bentonite cutoff walls using the piezocone penetration test[J]. Soils and Foundations, 2016, 56(2): 277-290.
[10]	ABBASLOU H, GHANIZADEH A R, AMLASHI A T. The compatibility of bentonite/sepiolite plastic concrete cut-off wall material[J]. Construction and Building Materials, 2016, 124: 1165-1173.
[11]	KERAMATIKERMAN M, CHEGENIDEH A, NIKRAAZ H. An investigation into effect of sawdust treatment on permeability and compressibility of soil-bentonite slurry cut-off wall[J]. Journal of Cleaner Production, 2017, 162: 1-6.
[12]	SAEEDI M, LI L Y, GRACE J R. Desorption and mobility mechanisms of co-existing polycyclic aromatic hydrocarbons and heavy metals in clays and clay minerals[J]. Journal of Environmental Management, 2018, 214: 204-214.
[13]	谢婷, 孟昭福, 路浩源, 等. BS+DAS复配修饰膨润土吸附Cr(Ⅵ)和Cd2+的研究[J]. 环境科学学报, 2018, 38(7): 2833-2841.
[14]	LIN J, JIANG B, ZHAN Y. Effect of pre-treatment of bentonite with sodium and calcium ions on phosphate adsorption onto zirconium-modified bentonite[J]. Journal of Environmental Management, 2018, 217: 183-195.
[15]	邵红, 刘相龙, 李云姣, 等. 两种改性膨润土对含油废水吸附行为的研究[J]. 环境科学学报, 2015, 35(7): 2114-2120.
[16]	REGADIO M, RUIZ A I, RODRIGUEZ-RASTRERO M, et al. Containment and attenuating layers: An affordable strategy that preserves soil and water from landfill pollution[J]. Waste Management, 2015, 46: 408-419.
[17]	陈宁, 王海滨, 刘树信. 空心粉煤灰对铁氧体-炭黑/水泥基复合材料吸波性能的影响[J]. 复合材料学报, 2017, 34(6): 1381-1387.
[18]	赵庆圆, 李小明, 杨麒, 等. 磷酸盐、腐殖酸与粉煤灰联合钝化处理模拟铅镉污染土壤[J]. 环境科学, 2018, 39(1): 389-398.
[19]	朱双, 盛广宏, 王铖铖, 等. 粉煤灰/氧化石墨烯复合材料吸附Hg(Ⅱ)[J]. 环境工程学报, 2017, 11(3): 1857-1864.
[20]	唐振平, 毕玉玺, 刘迎九, 等. 氧化石墨烯/有机改性膨润土复合材料的制备及其对Cd(Ⅱ)的吸附[J]. 复合材料学报, 2018, 35(11): 3196-3204.
[21]	陈婧, 谢水波, 曾涛涛, 等. 羟基铁插层膨润土的制备及其对铀(VI)的吸附特性与机制[J]. 复合材料学报, 2016, 33(11): 2649-2656.
[22]	何士冲. 复杂体系下有机膨润土吸附性能及垃圾填埋防渗性能基础研究[D]. 杭州: 浙江大学, 2017.
[23]	张广兴, 邵红, 李云娇, 等. 复合改性膨润土对氨氮废水的吸附及脱附[J]. 环境工程学报, 2017, 11(3): 1494-1500.
[24]	XU H, ZHU W, QIAN X, et al. Studies on hydraulic conductivity and compressibility of backfills for soil-bentonite cutoff walls[J]. Applied Clay Science, 2016, 132-133: 326-335.
[25]	杨玉玲. 六偏磷酸钠改良钙基膨润土系竖向隔离墙防渗控污性能研究[D]. 南京: 东南大学, 2017.
[26]	梅丹兵. 土-膨润土系竖向隔离工程屏障阻滞污染物运移的模型实验研究[D]. 南京: 东南大学, 2017.
[27]	文一多. 砂土/粉土-膨润土防污隔离墙渗透性的室内和现场实验研究[D]. 杭州: 浙江大学, 2017.
[28]	童星. 土-膨润土力学水力特性及其隔离墙的固结行为研究[D]. 杭州: 浙江大学, 2017.
[29]	曹守坤. 粉煤灰改性及处理含磷废水研究[D]. 泉州: 华侨大学, 2012.
[30]	王召. 石灰石粉-粉煤灰-矿渣混凝土基本力学性能与粘结性能研究[D]. 徐州: 中国矿业大学, 2017.
[31]	潘倩. 土-膨润土竖向隔离墙力学行为及其对防污性能影响[D]. 杭州: 浙江大学, 2016.
[32]	邹成龙, 梁吉艳, 姜伟, 等. 改性膨润土吸附处理重金属离子的研究进展[J]. 安徽农业科学, 2017, 45(10): 53-55.
[33]	王福刚, 张佳慧, 于吉洋, 等. 不同水力梯度对渗透系数影响研究[J]. 实验技术与管理, 2015, 32(6): 25-28.
[34]	张林林. 黏土矿物对重金属Pb(Ⅱ)吸附特性研究[D]. 大连: 大连理工大学, 2012.
[35]	刘松玉, 詹良通, 胡黎明, 等. 环境岩土工程研究进展[J]. 土木工程学报, 2016, 49(3): 6-30.
[36]	周冰. 改性水泥-膨润土垂直阻截墙防渗性能和抗侵蚀能力的研究[D]. 长春: 吉林大学, 2013.

PDF下载( 2001 KB)XML下载导出引用Turn off MathJax -->
点击查看大图

计量

文章访问数:1316
HTML全文浏览数:1269
PDF下载数:129
施引文献:0

出版历程

刊出日期:2019-03-14

---

-->

粉煤灰-膨润土阻隔墙控制地下水中镉污染

黄琴琴^1,2,,
刘国^1,2,,
文梅燕^1,2,
叶长文^1,2,
刘晏辉^1,2,
曾燚^1,2
1.成都理工大学地质灾害防治与地质环境保护国家重点实验室，成都 610059
2.成都理工大学国家环境保护水土污染协同控制与联合修复重点实验室，成都 610059
基金项目: 四川省重点研发项目2018SZ0321 成都理工大学地质灾害防治与地质环境保护国家重点实验室自主研究课题SKLGP2016Z008四川省重点研发项目(2018SZ0321) 成都理工大学地质灾害防治与地质环境保护国家重点实验室自主研究课题(SKLGP2016Z008)
关键词: 镉污染防治/
阻隔墙/
粉煤灰资源化/
改性增强膨润土/
重金属物理吸附
摘要:为了探究以固体废弃物粉煤灰和吸附性强的膨润土为材料制备的阻隔墙对镉污染的控制效果，采用微观表征、渗透实验、吸附实验、穿透实验、单轴抗压实验和侵蚀实验研究阻隔墙的性能。结果表明：阻隔墙材料的最佳质量配比为粉煤灰∶膨润土=5∶1，水泥质量占整个体系的5%；所得阻隔墙的渗透系数为1.11×10-8 m·s-1；最大抗压强度291.97 kPa；复合材料最大吸附率为98.38%。同时发现，固化体系中膨润土填充在粉煤灰球体的空隙处和表面，粉煤灰和膨润土都与水泥产生了水化产物和胶结物，Cd2+附着在阻隔材料表面；阻隔墙吸附的系统符合准一级动力学模型和Freundlich方程；系统的总吸附速率受液膜扩散与颗粒扩散同时影响；阻隔墙对Cd2+作用以物理吸附为主；墙体的抗碱腐蚀性比抗酸腐蚀性、耐有机污染物腐蚀性强。该研究可为将阻隔墙技术应用于地下水污染场地提供理论依据。

English Abstract

全文HTML

--> --> --> 参考文献 (36)