Catalytic degradation of volatile organic compounds over Cr-Ce/Al2O3 catalysts
GE Weilin1,2,3,,QIAN Jinze1,2,3,
XU Siyao1,2,3,
LI Sen1,2,3
1.Shanghai Research Institute of Chemical Industry Co.Ltd., Shanghai 200062,China
2.State Key Laboratory of Polyolefins and Catalysis, Shanghai 200062,China
3.Shanghai Key Laboratory of Catalysis Technology for Polyolefins, Shanghai 200062,China
-->
摘要
HTML全文
图
参考文献
相关文章
施引文献
资源附件
访问统计
摘要:采用共沉淀法制备了一系列不同铬铈负载量和铬铈负载比例的Cr-Ce/Al2O3催化剂,采用XRD、BET、NH3-TPD以及H2-TPR对所制得的催化剂进行表征。在空速为15 000 h-1、挥发性有机物体积分数为1 500 μL·L-1的条件下,于固定床反应器上考察了催化剂在三氯乙烯(TCE)催化氧化降解反应中的催化活性。实验结果表明,Cr-Ce/Al2O3(5%,10%)系列催化剂具有较好的低温催化降解三氯乙烯活性,其中Cr-Ce/Al2O3(5%,10%)活性最高,在271.3 ℃时可将尾气中90%的三氯乙烯降解。催化剂反应800 min后活性仅有轻微下降,说明该催化剂具有较好的稳定性。此外,将该催化剂用于其他VOCs催化降解反应中同样具有较好的活性,在350 ℃时可以将尾气中VOCs完全降解。
关键词: 催化降解/
挥发性有机物/
三氧化二铝/
铬铈氧化物
Abstract:A series of Cr-Ce/Al2O3 catalysts with different amount and ratio of Cr-Ce oxides were prepared by coprecipitation method, the obtained catalysts were characterized by XRD, BET, NH3-TPD and H2-TPR. The catalytic activity of these catalysts were tested for catalytic oxidation of trichloroethylene(TCE) on a fixed bed reactor with a GHSV of 15 000 h-1 and VOCs volume fraction of 1 500 μL·L-1. The results revealed that Cr-Ce/Al2O3 catalysts present high catalytic activity for the low temperature catalytic oxidation of TCE, and Cr-Ce/Al2O3(5%, 10%) catalyst is identified as the most active catalyst, and 90% of trichloroethylene degradation at 271.3 ℃. The activity of the catalyst after 800 min reaction only slightly decreased, indicating that the catalyst has good stability. In addition, the catalyst used to catalyze the degradation of other VOCs has the same good activity, and the exhaust gas can be completely degraded VOCs at 350 ℃.
Key words:catalytic degradation/
volatile organic compounds/
Al2O3/
Cr-Ce mixed oxide.
| [1] | 张广宏,赵福真,季生福,等.挥发性有机物催化燃烧消除的研究进展[J].化工进展, 2007,6(5):624-631 |
| [2] | PIUMETTI M, FINO D, RUSSO N.Mesoporous manganese oxides prepared by solution combustion synthesis as catalysts for the total oxidation of VOCs[J].Applied Catalysis B: Environmental,2015,3:277-287 |
| [3] | ALBERICI R M, JARDIM W F.Photocatalytic destruction of VOCs in the gas-phase using titanium dioxide[J].Applied Catalysis B: Environmental,1997,4:55-68 |
| [4] | TANG W X, WU X F, LI D Y, et al.Oxalate route for promoting activity of manganese oxide catalysts in total VOCs oxidation: Effect of calcination temperature and preparation methods[J].Journal of Materials Chemistry A,2014,2(8):2544-2554 |
| [5] | SANZ O, DELGADO J J, NAVARRO P, et al.VOCs combustion catalysed by platinum supported on manganese octahedral molecular sieves[J].Applied Catalysis B: Environmental,2011,0:231-237 |
| [6] | 董建民,孙海霞,马涛,等.贵金属催化燃烧催化剂的研究[J].当代化工, 2016,5(4):720-723 |
| [7] | KIM S C, SHIM W G.Catalytic combustion of VOCs over a series of manganese oxide catalysts[J].Applied Catalysis B: Environmental,2010,8:180-185 |
| [8] | NIE A M, YANG H S, LI Q, et al.Catalytic oxidation of chlorobenzene over V2O5/TiO2-carbon nanotubes composites[J].Industrial & Engineering Chemistry Researech,2011,0(17):9944-9948 |
| [9] | KAWI S, TE M.MCM-48 supported chromium catalyst for trichloroethylene oxidation[J].Catalysis Today,1998,4(1):101-109 |
| [10] | DAI Q G, WANG X Y, LU G Z.Low-temperature catalytic combustion of trichloroethylene over cerium oxide and catalyst deactivation[J].Applied Catalysis B: Environmental,2008,1(3):192-202 |
| [11] | HUANG Q Q, MENG Z H, ZHOU R X.The effect of synergy between Cr2O3-CeO2 and USY zeolite on the catalytic performance and durability of chromium and cerium modified USY catalysts for decomposition of chlorinated volatile organic compounds[J].Applied Catalysis B: Environmental,2012,5:179-189 |
| [12] | 钱金泽,李森,罗勇,等.铬改性分子筛催化降解三氯乙烯研究[J].环境科学学报, 2016,6(9):3419-3427 |
| [13] | 钱金泽,李森,罗勇,等.Cr-Ce氧化物改性 H-MOR分子筛催化氧化降解三氯乙烯的研究[J].精细化工,2016,3(7):779-786 |
| [14] | WU M, WANG X Y, DAI Q G.Catalytic combustion of chlorobenzene over Mn-Ce/Al2O3 catalyst promoted by Mg[J].Catalysis Communications,2010,1(12):1022-1025 |
| [15] | STERE C, ADRESS W, BURCH R.Ambient temperature hydrocarbon selective catalytic reduction of NOx using atmospheric pressure nonthermal plasma activation of a Ag/Al2O3 catalyst[J].ACS Catalysis,2014,4(2):666-673 |
| [16] | LYU L, ZHANG L L, WANG Q Y, et al.Enhanced fenton catalytic efficiency of γ-Cu-Al2O3 by σ-Cu2+-ligand complexes from aromatic pollutant degradation[J].Environmental Science & Technology,2015,9(14):8639-8647 |
| [17] | QIAO A, KALEVARU VN, RADNIK J, et al.Oxidative dehydrogenation of ethane to ethylene over V2O5/Al2O3 catalysts: Effect of source of alumina on the catalytic performance[J].Industrial & Engineering Chemistry Researech,2014,3(49):18711-18721 |
| [18] | LIU G, ZENG L, ZHAO Z J, et al.Platinum-modified ZnO/Al2O3 for propane dehydrogenation: Minimized platinum usage and improved catalytic stability[J].ACS Catalysis,2016,6(4):2158-2162 |
| [19] | WU M, WANG X Y, DAI Q G, et al.Low temperature catalytic combustion of chlorobenzene over Mn-Ce-O/γ-Al2O3 mixed oxides catalyst[J].Catalysis Today,2010,8(3):336-342 |
| [20] | FENG X P, GAO C J, GUO Z J, et al.Pore structure controllable synthesis of mesoporous poly(ionic liquid)s by copolymerization of alkylvinylimidazolium salts and divinylbenzene[J].RSC Advances,2014,4(45):23389-23395 |
| [21] | DUMITRIU E, HULEA V.Effects of channel structures and acid properties of large-pore zeolites in the liquid-phase tert-butylation of phenol[J].Journal of Catalysis,2003,8(2):249-257 |
| [22] | WANG X Y, KANG Q, LI D.Low-temperature catalytic combustion of chlorobenzene over MnOx-CeO2 mixed oxide catalysts[J].Catalysis Communications,2008,9(13):215-216 |
| [23] | DE R B, LPEZ-FONSECA R, GONZLEZ-VELASCO J R, et al.On the mechanism of the catalytic destruction of 1,2-dichloroethane over Ce/Zr mixed oxide catalysts[J].Journal of Molecular Catalysis A:Chemistry,2007,8(1):181-188 |
| [24] | WANG X, XIE Y C.Total oxidation of CH4 on Sn-Cr composite oxide catalysts[J].Applied Catalysis B: Environmental,2001,5(2):85-94 |
| [25] | 孟中华,杨鹏,周仁贤.铈铬比例对CeO2-CrOx复合氧化物催化剂上1,2-二氯乙烷催化氧化性能的影响[J].物理化学学报,2013,9(2):391-396 |
| [26] | COSTA C N, CHRISTOU S Y, GEORGIOU G, et al.Mathematical modeling of the oxygen storage capacity phenomenon studied by CO pulse transient experiments over Pd/CeO2 catalyst[J].Journal of Catalysis,2003,9(2):259-272 |
Turn off MathJax -->
点击查看大图计量
文章访问数:1278
HTML全文浏览数:765
PDF下载数:483
施引文献:0
出版历程
刊出日期:2018-02-08
-->
Cr-Ce/Al2O3催化剂对挥发性有机物的催化降解
葛伟林1,2,3,,钱金泽1,2,3,
徐思遥1,2,3,
李森1,2,3
1.上海化工研究院有限公司,上海 200062
2.聚烯烃催化技术与高性能材料国家重点实验室,上海 200062
3.上海市聚烯烃催化技术重点实验室,上海 200062
基金项目:
关键词: 催化降解/
挥发性有机物/
三氧化二铝/
铬铈氧化物
摘要:采用共沉淀法制备了一系列不同铬铈负载量和铬铈负载比例的Cr-Ce/Al2O3催化剂,采用XRD、BET、NH3-TPD以及H2-TPR对所制得的催化剂进行表征。在空速为15 000 h-1、挥发性有机物体积分数为1 500 μL·L-1的条件下,于固定床反应器上考察了催化剂在三氯乙烯(TCE)催化氧化降解反应中的催化活性。实验结果表明,Cr-Ce/Al2O3(5%,10%)系列催化剂具有较好的低温催化降解三氯乙烯活性,其中Cr-Ce/Al2O3(5%,10%)活性最高,在271.3 ℃时可将尾气中90%的三氯乙烯降解。催化剂反应800 min后活性仅有轻微下降,说明该催化剂具有较好的稳定性。此外,将该催化剂用于其他VOCs催化降解反应中同样具有较好的活性,在350 ℃时可以将尾气中VOCs完全降解。
English Abstract
Catalytic degradation of volatile organic compounds over Cr-Ce/Al2O3 catalysts
GE Weilin1,2,3,,QIAN Jinze1,2,3,
XU Siyao1,2,3,
LI Sen1,2,3
1.Shanghai Research Institute of Chemical Industry Co.Ltd., Shanghai 200062,China
2.State Key Laboratory of Polyolefins and Catalysis, Shanghai 200062,China
3.Shanghai Key Laboratory of Catalysis Technology for Polyolefins, Shanghai 200062,China
Keywords: catalytic degradation/
volatile organic compounds/
Al2O3/
Cr-Ce mixed oxide
Abstract:A series of Cr-Ce/Al2O3 catalysts with different amount and ratio of Cr-Ce oxides were prepared by coprecipitation method, the obtained catalysts were characterized by XRD, BET, NH3-TPD and H2-TPR. The catalytic activity of these catalysts were tested for catalytic oxidation of trichloroethylene(TCE) on a fixed bed reactor with a GHSV of 15 000 h-1 and VOCs volume fraction of 1 500 μL·L-1. The results revealed that Cr-Ce/Al2O3 catalysts present high catalytic activity for the low temperature catalytic oxidation of TCE, and Cr-Ce/Al2O3(5%, 10%) catalyst is identified as the most active catalyst, and 90% of trichloroethylene degradation at 271.3 ℃. The activity of the catalyst after 800 min reaction only slightly decreased, indicating that the catalyst has good stability. In addition, the catalyst used to catalyze the degradation of other VOCs has the same good activity, and the exhaust gas can be completely degraded VOCs at 350 ℃.