\r董岸杰^{1, 2}，张朋生¹，叶展鹏¹，邓联东¹，张建华¹

AuthorsHTML:\r董岸杰^{1, 2}，张朋生¹，叶展鹏¹，邓联东¹，张建华¹

AuthorsListE:\rDong Anjie^{1, 2}，Zhang Pengsheng¹，Ye Zhanpeng¹，Deng Liandong¹，Zhang Jianhua¹


AuthorsHTMLE:\rDong Anjie^{1, 2}，Zhang Pengsheng¹，Ye Zhanpeng¹，Deng Liandong¹，Zhang Jianhua¹


Unit:\r1. 天津大学化工学院，天津 300072；
2. 天津化学化工协同创新中心，天津 300072



Unit_EngLish:\r1．School of Chemical Engineering and Technology，Tianjin University，Tianjin 300072，China；
2．Collaborative Innovation Center of Chemical Science and Engineering(Tianjin)，Tianjin 300072，China


Abstract_Chinese:\r针对水下涂层材料在使用过程中产生的微裂纹难以及时修复和海洋生物污损问题，设计开发了一种氟化聚合物/双微胶囊的环氧树脂复合涂层(PFG/Dual-MCs/ER)，该复合涂层具有微裂纹自修复和抗生物黏附的双重功能．采用原位乳液聚合法制备了包裹环氧树脂和稀释剂的聚脲醛微胶囊(ER-MCs)，采用溶剂蒸发法制备了包裹水下环氧固化剂的聚甲基丙烯酸甲酯微胶囊(UEH-MCs)，采用自由基聚合法制备了甲基丙烯酸六氟丁酯(HFBM)与甲基丙烯酸缩水甘油酯(GMA)的无规共聚物(PFG)．将两种微胶囊包埋在环氧树脂涂层中并在表面接枝上PFG，制备出PFG/Dual-MCs/ER 复合涂层．表征了微胶囊和PFG 的结构组成，并检测了涂层的自修复和抗蛋白黏附性能．结果表明，PFG/Dual-MCs/ER 复合涂层具有较好的自修复能力，表面接枝PFG 使涂层表面对牛血清白蛋白的吸附明显减少．因此，这种兼具自修复和抗蛋白黏附性能，易于制备的PFG/Dual-MCs/ER 复合涂层在海洋设施防护领域具有较好的应用前景．


Abstract_English:\rA dual-function coating with self-healing and antibiofouling properties was prepared by combining two kinds of microcapsules in epoxy coating and surface grafting with fluorinated polymer to resolve the problems of microcracking and marine biofouling of underwater coating materials. A microcapsule，named ER-MCs，with a poly(urea-formaldehyde)shell，entrapped in a mixture of epoxy resin(E44)and n-butyl glycidyl ether was prepared using in-situ emulsion polymerization．Another microcapsule，named UEH-MCs，with a polymethyl methacrylate shell，entrapped in an underwater epoxy hardener(UEH)was prepared using a solvent evaporation technique．A
fluorinated polymer(PFG)was synthesized by conventional free radical polymerization using hexafluorobutyl methacrylate and glycidyl methacrylate as monomers．The two microcapsules were entrapped in the epoxy resin to form a self-healing Dual-MCs/ER coating and whereas PFG/Dual-MCs/ER coating was obtained by casting PFG solution on the incomplete cured surface of the Dual-MCs/ER．The structures of microcapsules and PFG were characterized and self-healing and anti-protein-fouling properties were detected．The results showed that the PFG/Dual-MCs/ER composite coating featured a desirable self-healing capability whereas the grafting of PFG on the surface of Dual-MCs/ER coating significantly reducd the adsorption of bovine serum albumin on the coating surface. Therefore，given its easy fabrication，the PFG/Dual-MCs/ER composite coating，which possesses self-healing and anti-protein-fouling properties，features a promising application in the field of marine facility protection.



Keyword_Chinese:微胶囊；自修复；氟化聚合物；防污涂层


Keywords_English:microcapsule；self-healing；fluorinated polymer；antifouling coating