外文题目: Tb3Al2.5Ga2.5O12 Transparent Ceramic for Magneto-Optical Application
作者: Hao, Deming; Zhou, Shengming; Feng, Yue; Tang, Yanru; Yi, Xuezhuan; Zhang, Shuai; Chen, Chong; Lin, Hui
刊名: Int. J. Appl. Ceram. Technol.
年: 2016 卷: 13 期: 5 页： 816--820
英文关键词:
Tb3Ga5-xAlxO12; transparent ceramic; magneto-optical material; Verdet constant
TERBIUM ALUMINUM GARNET; FARADAY ROTATOR; SINGLE-CRYSTAL; TAG CERAMICS; TB3AL5O12; GROWTH; FIBER
英文摘要:
The optical quality and microstructure of the Tb3Al2.5Ga2.5O12 transparent ceramic were investigated and compared with those of Tb3Ga5O12 (TGG) and Tb3Al5O12 (TAG). The transmission of the Tb3Al2.5Ga2.5O12 ceramic was as high as 80% in the visible and near-infrared (IR) regions, which was close to the theoretical value. The Verdet constant of the Tb3Al2.5Ga2.5O12 ceramic measured at 632.8 nm and room temperature was -150.6 rad/Tm, which was 12% larger than that of the TGG single crystal and 13% smaller than that of the TAG single crystal, and the Tb3Al2.5Ga2.5O12 ceramic showed the highest transparency among these three samples.


文献类型: 期刊论文
正文语种: English
收录类别: SCIEI
DOI: 10.1111/ijac.12565


全文传递服务