外文题目: Granulation of Y2O3 powders by a vibration method for the preparation of transparent ceramics
作者: Li, Xiaokai; Xu, Yangyang; Mao, Xiaojian; Zhu, Qiangqiang; Feng, Minghui; Jiang, Benxue; Zhang, Long
刊名: RSC Adv.
年: 2016 卷: 6 期: 107 页: 105755--105760
英文关键词:

FABRICATION; YTTRIA; ALUMINA; DENSITY; HIP
英文摘要:
A modified vibrating screen method was employed to prepare granulated Y2O3 powders, which were used to fabricate transparent ceramics. The granulation process was carried out with yttrium-stabilized zirconia balls (5 mm in diameter) in a 200-mesh screen, which was vibrated by a Heidolph shaker. After passage through the vibrating screen, the sub-micron Y2O3 particles were converted into large granules and collected in the bottom chamber of the sieve. Compared with the original powders, the granulated powders had a smaller repose angle of 34.09 degrees and larger apparent and tap densities with sharp rises of 50.54 and 32.07%, respectively, indicating a good flowability and filling properties. A high transmittance of 82% at 2500 nm was achieved for ceramics prepared using the granulated powders by vacuum sintering and hot isostatic pressing (HIP).


文献类型: 期刊论文
正文语种: English
收录类别: SCIEI
DOI: 10.1039/c6ra21799k


全文传递服务
相关话题/英文 文献 外文 语种 题目