荷载频率对结构钢及其焊接节点疲劳寿命的影响

本站小编 Free考研考试/2022-02-13

DOI: 10.11908/j.issn.0253-374x.20334

作者:

作者单位: 1.同济大学 土木工程学院,上海 200092;2.同济大学浙江学院,浙江 嘉兴 314051;3.中铁上海设计院集团有限公司,上海 200070


作者简介: 童乐为(1961—),男,教授,博士生导师,工学博士,主要研究方向为钢结构和组合结构。 E-mail:tonglw@tongji.edu.cn


通讯作者: 颜 阳(1987—),男,工程师,工学硕士,主要研究方向为钢结构和组合结构研发与设计。 E-mail:yanyang@sty.sh.cn

中图分类号: TU502+.6


基金项目: 国家自然科学基金面上项目(51778457);浙江省嘉兴市公益性研究计划项目(2020AY10030);中铁上海院集团科研计划(集-20-63)




Effect of Loading Frequency on Fatigue Life of Structural Steel and Welded Connection
Author:

Affiliation: 1.College of Civil Engineering, Tongji University, Shanghai 200092, China;2.Tongji Zhejiang College, Jiaxing 314051, China;3.China Railway Shanghai Design Institute Group Co., Ltd.,Shanghai 200070, China


Fund Project:




摘要
| 图/表
| 访问统计
| 参考文献
|相似文献
| 引证文献
| 资源附件

摘要:钢结构的高周疲劳试验研究采用低频、中频和高频加载,疲劳寿命是否会有差别或者有怎样的差别一直是试验者希望找到答案的问题。以结构钢及其焊接件为对象,对低频(30Hz以内)与中高频(100Hz左右)加载的疲劳试验数据(包括作者和其他****成果)进行分析对比,研究低频与中高频加载对疲劳寿命的影响,疲劳试验涉及高强钢Q460板材及其对焊节点、普钢Q345对焊节点。研究发现,低频与中高频加载的疲劳寿命有很大的差别,无论是钢材还是对焊节点,低频加载比中高频加载的疲劳寿命长或疲劳强度高。对这种现象的机理进行解释。建议对承受低频疲劳荷载的工程钢结构,其疲劳试验应符合实际采用低频疲劳试验机加载。若采用高于低频的疲劳试验机加载,则会显著地低估疲劳寿命。



Abstract:Is there any difference or what difference is in fatigue life between high-cycle fatigue tests of steel structures at the loading with low, medium, and high frequencies has always been a question for experimenters to find an answer to. Comparative analysis of fatigue test data (including tests conducted by the authors of the present paper and other scholars) was performed for structural steel as well as weldment at loadings between low frequency (below 30Hz) and medium-high frequency (around 100Hz). The effects of low and medium-high frequency loadings on fatigue life was investigated. The fatigue tests dealt with high strength steel Q460 and its butt-welded joints, as well as butt-welded joints of normal strength steel Q345. It was found that there was substantial difference in fatigue life between low and medium-high frequency loadings. The former had a longer fatigue life or higher fatigue strength than the latter, whether it was steel or butt-welded joints. The mechanism for this phenomenon was also explained. It is suggested that for engineering steel structures subjected to low frequency fatigue loadings, fatigue tests should be conducted using low frequency fatigue testing machine. It may significantly underestimate fatigue life if a fatigue testing machine with a frequency higher than low frequency is used.