Author NameAffiliation
Xiaonan YangSchool of Environment, Harbin Institute of Technology, Harbin 150090, China
Dongmei LiuSchool of Environment, Harbin Institute of Technology, Harbin 150090, China
Fuyi CuiCollege of Urban Construction and Environmental Engineering, Chongqing University, Chongqing 400044, China
Abstract:
At present, a growing number of consumer products contain engineered nanoparticle TiO2 (nano-TiO2), which has resulted in the consequences of nano-TiO2 entering the aquatic environment directly or indirectly at some stage. The fate of nano-TiO2 in the aquatic environment has become the key factor which affects its safety application and nanoecotoxicology. This paper aims to investigate how the dissolved organic matters (DOM), especially the molecular weight fractions in the aquatic environment, affect the aggregation, stability, and fate of nano-TiO2, and the interaction mechanism of DOM and nano-TiO2. Results of dynamic light scattering (DLS) showed that the molecular weight of DOM molecules caused different aggregation rates of nano-TiO2 in aqueous solution. Fourier Transform infrared spectroscopy (FTIR) results indicated the molecular structure is characteristics of DOM fractions and the mechanisms of bonds formation between DOM and nano-TiO2. Results of three-dimensional excitation-emission matrices (3D-EEM) confirmed the FTIR results and implied the increase of the stability of the π-π conjugated system in the presence of DOM. In addition, low molecular weight of DOM fractions appeared to show more affinity with nano-TiO2 than high molecular weight fractions.
Key words:titanium dioxide nanoparticlesdissolved organic matterdifferent molecular weight organics
DOI:10.11916/j.issn.1005-9113.19002
CLC NUMBER:X592
Fund:
Xiaonan Yang, Dongmei Liu, Fuyi Cui. Effect of Dissolved Organic Matter on Titanium Dioxide Nanoparticles in Aquatic Environment: Molecular Weight Fractions[J]. Journal of Harbin Institute of Technology (New Series), 2020, 27(5): 38-48. DOI: 10.11916/j.issn.1005-9113.19002
![复制到剪切板](images/copy.gif)
Fund Sponsored by the National Natural Science Foundation of China (Grant No. 51408162), the Special Financial Grant from the China Postdoctoral Science Foundation (Grant No. 2016T90303), the China Postdoctoral Science Foundation (Grant No. 2014M551258), and the Heilongjiang Province Postdoctoral Science Foundation (Grant No. LBH-Z14077) Corresponding author Xiaonan Yang, E-mail: xiaonanyang@hit.edu.cn
Fuyi Cui, E-mail: cuifuyi@hit.edu.cn Article history Received: 2019-01-06
ContentsAbstractFull textFigures/TablesPDF
Effect of Dissolved Organic Matter on Titanium Dioxide Nanoparticles in Aquatic Environment: Molecular Weight Fractions
Xiaonan Yang1
![Corresponding author](images/REcor.gif)
![xiaonanyang@hit.edu.cn](images/REemail.gif)
![Corresponding author](images/REcor.gif)
![cuifuyi@hit.edu.cn](images/REemail.gif)
1. School of Environment, Harbin Institute of Technology, Harbin 150090, China;
2. College of Urban Construction and Environmental Engineering, Chongqing University, Chongqing 400044, China
Received: 2019-01-06
Sponsored by the National Natural Science Foundation of China (Grant No. 51408162), the Special Financial Grant from the China Postdoctoral Science Foundation (Grant No. 2016T90303), the China Postdoctoral Science Foundation (Grant No. 2014M551258), and the Heilongjiang Province Postdoctoral Science Foundation (Grant No. LBH-Z14077)
Corresponding author: Xiaonan Yang, E-mail: xiaonanyang@hit.edu.cn;
Fuyi Cui, E-mail: cuifuyi@hit.edu.cn.
Abstract: At present, a growing number of consumer products contain engineered nanoparticle TiO2 (nano-TiO2), which has resulted in the consequences of nano-TiO2 entering the aquatic environment directly or indirectly at some stage. The fate of nano-TiO2 in the aquatic environment has become the key factor which affects its safety application and nanoecotoxicology. This paper aims to investigate how the dissolved organic matters (DOM), especially the molecular weight fractions in the aquatic environment, affect the aggregation, stability, and fate of nano-TiO2, and the interaction mechanism of DOM and nano-TiO2. Results of dynamic light scattering (DLS) showed that the molecular weight of DOM molecules caused different aggregation rates of nano-TiO2 in aqueous solution. Fourier Transform infrared spectroscopy (FTIR) results indicated the molecular structure is characteristics of DOM fractions and the mechanisms of bonds formation between DOM and nano-TiO2. Results of three-dimensional excitation-emission matrices (3D-EEM) confirmed the FTIR results and implied the increase of the stability of the π-π conjugated system in the presence of DOM. In addition, low molecular weight of DOM fractions appeared to show more affinity with nano-TiO2 than high molecular weight fractions.
Keywords: titanium dioxide nanoparticlesdissolved organic matterdifferent molecular weight organics
1 Introduction The global production of nanosized TiO2 has been applied in various fields such as semiconductors[1], cosmetics, electronics, food packaging materials[2], pigment, antimicrobial applications, catalysts, medical, and energy storage[3]. Besides, many nanomaterials (e.g., nanoabsorbent and nanocatalyst[4-5]) are being used for water purification and environment remediation. Given the increasing production, the questions that the consequences of nano-TiO2 entering the environment especially the aquatic environment[6-8] at some stage have been raised. Thus, the potential release in the environment and the subsequent effects on ecosystem health are becoming researchers' concerns[6, 9-13].
With high surface area, TiO2 nanoparticles (NPs) are capable of absorbing various contaminants from aquatic environments and may form nanopollutants complexes. Strong evidence has shown that nano-TiO2 is toxic to aquatic species, algae, cell, and microorganisms[14-17]. The special characteristics of NPs, such as particle size, the surface parameters, charge and chemical reactivity, are vital to determine the toxic effects of NPs[18]. Therefore, characteristics of nano-TiO2 and their fate in the environment are necessary to be quantified in exposure scenarios. Besides, differences in speciation with dissolved colloidal organics in aquatic environment are also worthy to be noted, which, unfortunately, are often ignored. In the meantime, due to the strong hydrophobic interaction of individual nano-TiO2 in aqueous phase, they may aggregate and deposit[19-20]. Thus, the size distribution and surface physicochemistry (including coatings produced by natural colloids) of NPs are primary to understand their ecotoxicology. Clearly, it is essential to thoroughly understand the nano-TiO2 behavior in the aqueous phase with the speciation of dissolved organic matters (DOMs).
DOM is a ubiquitous natural colloid, which plays a critical role in the biogeochemical cycling of trace metals and the mobility of colloidal particles in aquatic environments[21-24]. Meanwhile, dissolved colloidal organics consisting of a complex and heterogeneous continuum of high-to low-molecular weight species exhibit different water solubilities and reactivities[25]. Although the effects of DOM on the aggregation of NPs have been confirmed[1], limited information is available about how the fractionated colloidal organics of DOM interact with NPs in natural aqueous environment and the mechanisms of the interaction. Therefore, it is important to study the adsorption behaviors of different molecular weight DOM fractions with nano-TiO2, which can be employed to assess and predict the influences of DOM on the transport, transformations, bioavailability, and nanotoxicity of nano-TiO2 in the aqueous environment.
The objective of this study is to investigate the effect of different molecular weight DOM fractions on the interaction behavior and mechanisms of nano-TiO2 and DOM in aqueous phase. Three issues are addressed in this research: 1) the particle distributions of these four fractions under the simulated natural aqueous condition; 2) the dynamic light scattering (DLS) and electrophoretic mobility characteristics of fractionated DOM with nano-TiO2; and 3) the characterization of the interaction mechanism between DOM fractions and nano-TiO2 by fingerprint of molecular structure.
2 Materials and Methods 2.1 Characterization of nano-TiO2 and Suspension Preparation The rutile titanium oxide (15 wt% titanium oxide in water, Average Particle Size (APS): 5-30 nm, CAS #: 1317-80-2) in water was purchased from Nanostructured & Amorphous Materials, Inc. nano-TiO2 concentration of stock suspension is 500 mg/L NPs dissolved in the ultrapure water (18.2 MΩ/cm Millipore, Billerica, MA, USA). To ensure the homogeneity dispersity, it was sonicated (Branson Sonifier W-250D, 25 W at 10% energy input) for 20 mins before each experiment.
Transmission electron microcopy (TEM, JEOL Japan) was employed to characterize the morphology, structure, and particle size of nano-TiO2 at 100 kV[26]. TEM samples were prepared by dropping 5 μL of the nano-TiO2 suspension on the 200 mesh copper grids (a continuous carbon film coating) and dried at room temperature. Particle size distributions (PSDs) of nano-TiO2 were determined by using a Zetasizer Nano ZS (Malvern Instruments, U.K.) DLS. Suspensions were agitated vigorously for 10 s by vortex mixer to ensure a representative sample DLS analysis. The point of zero charge (PZC) of nano-TiO2 was determined by electrophoretic mobility measurements.
2.2 Atomic Force Microscopy (AFM) AFM image was acquired in tapping mode by applying Nanoscope IIIb equipped with an extender and E-scanner (Bioscope, Santa Barbara, CA). Samples were deposited onto the mica (approximately 1 cm×1 cm), fixed on glass slides, and then dried in the ambient temperature. The morphology images were scanned by AFM in contact mode at a scan rate of 1 Hz.
2.3 Preparation and Characterization of DOM Fractions Humic acid sodium salt (CAS: 68131-04-4, sigma-aldrich) was dissolved in ultrapure water and adjusted to a final concentration of 10 mg/L. By applying the standard UF membranes with different molecular weight cut-off (Milipore, USA), the DOM solution was fractionized into four MW fractions: < 1 k (DOM1), 1-10 k (DOM2), 10-100 k (DOM3), and 100 k-0.45 μm (DOM4). All the fractionated DOMs were dialyzed in a MW100 dialysis bag (MD77, MEMBRA-CEL ? Viskase) for 24 h on a magnetic stirring apparatus to reduce the interference of irrelevant ions. The operating pressures were 0.65 atm for membranes with an NMWL of 100 kDa, 1.1-1.3 atm for membranes with an NMWL of 10 kDa, and 1.3-2.2 atm for membranes with an NMWL of 1 kDa, which were slightly modified by the method in Ref. [27].
2.4 Spectroscopic Measurements Samples of the nano-TiO2 with fractionated colloid organics adsorption were investigated by Fourier Transform infrared spectroscopy (FTIR) spectrophotometer (Spectrum One, PerkinElmer). Each sample was first freeze-dried for 24 h, then blended with KBr to remove water, pressed into a thin disk, and immediately taken into the sample pool for the FTIR analysis. Ratios of the absorbance of DOMs at 465 and 665 nm (E4/E6 ratios) were determined under the condition of pH 7 with spectrophotometer (UV-2550, Shimadzu).
The three-dimensional excitation-emission matrices (3D-EEM) spectra of the solutions were recorded by scanning spectrofluorometer with a 150-W ozone-free Xenon arc lamp (Hitachi Model FP6500). All spectra were collected using Chen's method[28].
2.5 Batch Experiments Batch experiments were conducted to investigate the adsorption behavior of nano-TiO2 with fractionated DOMs. nano-TiO2 was added into a 100 mL flask which contained 10 mg/L of each fractionated DOM and PBS buffer solution under the condition of pH 7.0±0.1. The suspensions were shaken in water bath (25 ℃, 180 r/min). After 24 h, the solution samples were taken from each flask separately for the experiments of total organic carbon (TOC, TOC-VCPN SHIMADAZU), UV-visible spectrometer (UV759S, SHANGHAI JINGMI CO.), FTIR, and 3D-EEM. Meanwhile, controlled experiments were carried out without adding the nano-TiO2. All adsorption experiments were conducted at room temperature (23-25 ℃).
3 Results and Discussion 3.1 Characterization of nano-TiO2 in DOM-free Suspension Stable aqueous nano-TiO2 suspensions were formed with sample preparation protocols in Section 2.1. DLS results show that the average aggregated particle size of the nano-TiO2 was 198.3 nm (Fig. 1(b)), which was larger than the advertised label (30 nm). Meanwhile, the image of AFM (Fig. 1) presents that the nano-TiO2 was well dispersed in the DI water (pH 7) and its primary particle size showed consistent result with the DLS and TEM images. Electrophoretic mobility measurement results indicate that the nano-TiO2 had a PZC in pH 6.2±0.1 in the support information.
Fig.1
![Click to view original](PIC/jhit-27-5-38-1.jpg)
3.2 PSD of DOM Fractions Four different cumulative fractions, termed as UF1 (< 1 K), UF2 (1 K-0 K), UF3 (10 K-100 K), and UF4 (100 K), were obtained based on molecular weight, and the original DOM without fractionated was chosen as the control solution (UF0). Fig. 2(a) shows the particle distribution of the four fractions under 10 mg/L DOM concentration in pH 7. The average value of hydraulic radius was clearly in proportion to the molecular weight, which was 60 nm (UF1), 73.4 nm (UF2), 218.7 nm (UF3), and 676.6 nm (UF4), respectively. The morphology of these four fractions was observed with AFM (Fig. 2(b)), which was consistent with the results of DSL as shown in Fig. 1(a).
Fig.2
![Click to view original](PIC/jhit-27-5-38-2.jpg)
3.3 Spectroscopic Characteristics of DOM Fractions 3.3.1 FTIR In order to determine the interaction mechanism of nano-TiO2 with different fractionated DOMs, 3D-EEM spectrum, FTIR spectrum, and UV-Vis spectrum were employed. Characteristics of functional groups of the fractionated DOM were further investigated. As shown in Fig. 3, the results of FTIR for UF0, UF1, UF2, UF3, and UF4 were similar. The peak intensity of 3400 cm-1 was observed in four fractions, representing the stretching vibration of associated -OH. Also, all the weak peaks occurred at 3000-2800 cm-1 because of the stretching vibration of fat C-H bond. The peak of 1600 cm-1 indicated the overlapped peak of the skeleton vibration of aromatic ring C = C absorption, H bond association, and C = O absorption and amides bond[30]. Fingerprint bands of these functional groups showed similar characteristics in the FTIR spectrum. However, differences in FTIR track spectra were observed for the oxygen functional groups, i.e., stronger frequency at 1380 cm-1 and 1270 cm-1 for UF1 and UF2. Moreover, UF3 and UF4 had higher peak values than UF1 and UF2 at 2930 cm-1, representing more aliphatic chains[26, 31].
Fig.3
![Click to view original](PIC/jhit-27-5-38-3.jpg)
3.3.2 UV Spectroscopic The ratio of absorbance at 465 to 665 nm, commonly referred to as the E4/E6 ratios, represents a negative correlation between C content or reduced viscosity (molecular weight) and a positive correlation between E4/E6 and total acidity or O content[32], which is also an indicator of aromaticity[33-34]. As shown in Fig. 4, E4/E6 ratios of the four DOM fractions gradually decreased with the increasing molecular weight, providing further evidence to the highest level of aromaticity in UF1. The ratios of UF1 and UF2 were almost twice of UF3 and UF4, indicating that there were more chromophores functional groups in UF1 and UF2. It can be explained by the fact that the ratio of E4/E6 is affected by the relative abundance of ketonic C=O and aromatic C=C functional groups (or chromophores) as well as auxochromes such as C-OH and C-NH2. Moreover, the ketonic C=O functional groups exhibited a weaker absorption in the visible range, whereas the auxochromes did not confer color but increased the color of the chromophores[35-37].
Fig.4
![Click to view original](PIC/jhit-27-5-38-4.jpg)
3.3.3 3D-EEMs Three dimensional fluorescence spectroscopy is an analytical tool for probing the structural signatures of fluorescent functional groups (e.g., molecular size and content of aromatics, phenolics, carboxyl, and hydroxyl) by revealing fluorescence peak positioning and shift, peak intensity, and peak broadening[28, 38]. Each fraction of the DOMs showed a similar characteristic fluorescence that the major fluorophore occurred at peak at Ex/Em: 290/450 nm (Fig. 5). These peaks corresponded to humic-like structures that are classified as Type C (at Ex/Em: 330/450 nm)[39]. In addition, the peak intensity of lower MW range UF1 (from 969 a.u. to 668 a.u.) and UF2 (from 639 a.u. to 485 a.u.) were stronger than those of UF3 (110 a.u. to 75 a.u.) and UF4 (from 91 a.u. to 69 a.u.), indicating that the higher MW DOM has less fluorophore and weaker fluorescence intensity[40]. The proposed explanation for this phenomenon is the possibility of the transition from the ground state to the excited state, which enhanced the relatively short wavelengths of the fluorescence peak in the lower MW DOM (UF1 and UF2) compared with the higher MW DOM[41-42]. A possible reason of the weakened intensity of peaks in UF1, UF2, UF3, and UF4 fractions may be the fluorescent quenching effects resulting from the interaction of DOM and nano-TiO2.
Fig.5
![Click to view original](PIC/jhit-27-5-38-5.jpg)
3.4 Effect of the Fractionated DOM on the Stability of nano-TiO2 3.4.1 DLS According to the PZC of nano-TiO2 (SP), the condition pH value was chosen at 5 and 7. Fig. 6 shows the PSD of nano-TiO2 with four fractions of DOM at pH 7. The PSDs of UF1 and UF2 both increased, from 60 nm to 93.8 nm and 73.4 nm to 101.4 nm, respectively, while those of UF3 and UF4 slightly decreased from 218.7 nm to 191.5 nm and 676.6 nm to 584.9 nm. This could be the cause that there were more carboxyl groups in the lower MW fractions than in higher MW fractions which induced aggregation by ligand exchanges with nano-TiO2 in the UF1 and UF2. While in the UF3 and UF4 fractions, the stability of both suspensions was enhanced by the electrostatic repulsion effects and the PSD was reduced in the meantime. There are two possible reasons: one is that there was repulsive force owing to both nano-TiO2 and DOM fractions which presented negative charge in the pH 7 solutions; and the other is the less adsorption behavior in the suspensions of UF3 and UF4 with nano-TiO2 due to the less carboxyl groups in UF3 and UF4 fractions.
Fig.6
![Click to view original](PIC/jhit-27-5-38-6.jpg)
Besides, the PSD of nano-TiO2 with DOM fractions at pH 5 was investigated to reveal the effect of pH value on the stability of the four DOM fractions with nano-TiO2. Different results were obtained as shown in Fig. 7. The PSD of the four fractions increased after the addition of nano-TiO2 due to the aggregation. The resulted PSDs of UF1 (60 nm), UF2 (73.4 nm), UF3 (218.7 nm), and UF4 (676.6 nm) were 248.1 nm, 267.5 nm, 507.2 nm, and 971.3 nm, respectively. The cause might be the electrostatic attraction between DOM fractions and nano-TiO2 resulting from the positive charge of nano-TiO2. As aforementioned, due to the synergistic effect of ligand exchanges and the electrostatic attraction, the PSDs of UF1 and UF2 increased more significantly than those of UF3 and UF4.
Fig.7
![Click to view original](PIC/jhit-27-5-38-7.jpg)
3.4.2 Zeta potential There is a clear relationship between zeta potential and molecular weight at pH 7. The zeta potential of UF1, UF2, UF3, and UF4 was -13.8 mV, -19.3 mV, -24.0 mV, and -27.8 mV, respectively. With the addition of nano-TiO2, the zeta potential was decreased to -32.6 mV, -33.4 mV, -39.7 mV, and -42.0 mV. The cause might be the increasing negative charges in the suspension resulting from the negatively charged surface hydroxyl groups of nano-TiO2 by losing electron at pH 7. Under the condition of pH 5, similar results were obtained between zeta potential and molecular weight as shown in Fig. 8. However, each zeta potential of UF1, UF2, UF3, and UF4 increased to -15.7 mV, -19.3 mV, -19.7 mV, and -21.6 mV. The reasonable factor was the electrostatic attractions and the coordination reaction between negatively charged DOM fractions and nano-TiO2 as well as the -MOH2+ on the surface of nano-TiO2.
Fig.8
![Click to view original](PIC/jhit-27-5-38-8.jpg)
3.4.3 Interaction mechanism of fractionated DOM with nano-TiO2: Spectrum and fingerprinting characteristics 1) ??FTIR characteristics.
FTIR was applied to investigate the existence of ligand exchange/surface complexation between DOM and nano-TiO2 (Fig. 9). The absorbance bands (Fig. 9(a)) at 1022 cm-1, 1070 cm-1, and 1150 cm-1 were assigned to the Ti-O swing vibration in the four DOM fractions. However, the peak at 1270 cm-1 of UF1 and UF2 was assigned to the C-O stretching vibration of carboxylate functional group and O-H deformation vibration, indicating the ligand exchange of the COO- (DOM fractions) with surface hydroxyl groups (nano-TiO2)[43]. By comparing with the spectrum in Fig. 3, for all the DOM fractions, the stretching band of the associated hydroxyls slightly shifted to the low frequency accompanied with the broader absorbed band, suggesting the enhanced energy hydrogen bond and reduced frequency of -OH stretching vibration. The results were consistent with strengthened absorbed peak at 2430 cm-1[44]. Nevertheless, the absorbed peak at 1270 cm-1 of UF3 and UF4 did not show the shift compared with the nano-TiO2-free spectrum, while the peak at 2430 cm-1 of UF3 and UF4 that corresponded to the hydrogen bond was also strengthened for the same reason as previously stated. Additionally, peak position of different fractions indicated that the functional group of COO- was mostly responsible for this band in DOM, especially at low MW (UF1, UF2) (Fig. 9).
Fig.9
![Click to view original](PIC/jhit-27-5-38-9.jpg)
2) ??Fluorescence characteristics.
Fluorescence spectra could provide structural fingerprinted signatures of adsorption between DOM fractions and nano-TiO2. After the addition of nano-TiO2, changes of the fluorescence characteristics were observed. Strong evidences showed that the peak intensity was weakened and red shifts were found in four fractions, in which the peak of UF1 shifted from Ex/Em (nm) 285/440 to 310/440, UF2 from Ex/Em (nm) 290/450 to 315/450, UF3 from Ex/Em (nm) 290/450 to 350/450, and UF4 from Ex/Em (nm) 290/450 to 310/450, respectively (Fig. 10). These peaks corresponded to humic-like structures that are classified as Type C. In addition, the peak intensities of lower MW range UF1 (969 a.u. to 668 a.u.) and UF2 (639 a.u. to 485 a.u.) were stronger than those of UF3 (110 a.u. to 75 a.u.) and UF4 (91 a.u. to 69 a.u.), indicating that the higher MW range has less fluorophore and weaker fluorescence intensity. The reason for the weakened intensity may be the presence of nano-TiO2 in the ligand involving quench fluorescence by aggregations colloid system of DOM fractions and nano-TiO2, and similar result was also obtained in Ref. [45] with iron oxide NPs. In addition, 3D-EEM spectra of all four fractions displayed red-shifted trends, which implied the forming of hydrogen bond of the ligand and the reduction of the conjugation extent. These results were consistent with the FTIR results discussed in Section 1).
Fig.10
![Click to view original](PIC/jhit-27-5-38-10.jpg)
3.4.4 Adsorption affinity between DOM fractions and Nano-TiO2 The adsorption affinity of nano-TiO2 with DOM fractions was investigated under the conditions of pH 5 and pH 7. Fig. 11 shows the clear trends that the adsorption affinity with lower MW fractions (UF1 and UF2) was stronger than that with macromolecules (UF3 and UF4). The reasonable explanation for this is the more carboxyl groups in small molecules which have affinity with the surface hydroxyl groups of nano-TiO2 because of the ligand exchange interaction. This led to smaller molecules of DOM interacted with nano-TiO2 and they showed stronger adsorption affinity than macromolecules. In addition, all the fractions at pH 7 displayed weaker capacity than those at pH 5 because there were more -MOH2+ on the surface of nano-TiO2 absorbed by DOM fractions due to the electrostatic attracted interactions. In contrast, there was weaker affinity at pH 7 because the electrostatic repulsive forces dominated in the suspension for the same reason as stated in Section 3.4.2. It was found in Fig. 11 that there was little adsorption in UF3 and UF4 at pH 7 compared with UF1 and UF2. The possible reason may be the synergistic effect of the electrostatic repulsive forces and the weak affinity with less surface hydroxyl groups in UF3 and UF4.
Fig.11
![Click to view original](PIC/jhit-27-5-38-11.jpg)
3.5 Conclusion for Environmental Implications The results provide fundamental information for understanding the specific behavior of nano-TiO2 with DOM speciation fractions in natural water and give basic clues to remove nano-TiO2 in the process of drinking water treatment. It is also important to gain the knowledge of the interaction mechanism of nano-TiO2 and DOM subfractions to better understand the behavior of TiO2 NPs in the aquatic environment. This can be a key point for elucidating the mechanisms of electrostatic effect and ligand exchange governing adsorption of DOM (different molecular weights) to nano-TiO2. Owing to the oxygen-containing functional groups of carboxyl and phenolic hydroxyl, the lower MW DOM has the trendency to absorb nano-TiO2 other than the DOM macromolecules. Moreover, these molecules with lower weight and smaller size are relatively hydrophilic and not effectively removed by coagulation or adsorption. Such information may help to better predict the transport and the fate of nano-TiO2 associated with DOM in the natural environment, and provide beneficial information for removing nano-TiO2 in drinking water treatment.
4 Supplementary Materials 1) ??Fig.S1
S1
![Click to view original](PIC/jhit-27-5-38-S1.jpg)
2) ??MOH2 represents the compound which contain the -OH in Section 3.4.2.
References
[1] Colvin V L. The potential environmental impact of engineered nanomaterials. Nature Biotechnology, 2003, 21(10): 1166-1170. DOI:10.1038/nbt875 (
![](images/locate.gif)
[2] Hansen S F, Michelson E S, Kamper A, et al. Categorization framework to aid exposure assessment of nanomaterials in consumer products. Ecotoxicology, 2008, 17(5): 438-447. DOI:10.1007/s10646-008-0210-4 (
![](images/locate.gif)
[3] Kiser M A, Ryu H, Jang H, et al. Biosorption of nanoparticles to heterotrophic wastewater biomass. Water Research, 2010, 44(14): 4105-4114. DOI:10.1016/j.watres.2010.05.036 (
![](images/locate.gif)
[4] Dror-Ehre A, Adin A, Markovich G, et al. Control of biofilm formation in water using molecularly capped silver nanoparticles. Water Research, 2010, 44(8): 2601-2609. DOI:10.1016/j.watres.2010.01.016 (
![](images/locate.gif)
[5] Chang M C, Kang H Y. Remediation of pyrene-contaminated soil by synthesized nanoscale zero-valent iron particles. Journal of Environmental Science and Health, Part A, 2009, 44(6): 576-582. DOI:10.1080/10934520902784609 (
![](images/locate.gif)
[6] Nowack B, Bucheli T D. Occurrence, behavior and effects of nanoparticles in the environment. Environmental Pollution, 2007, 150(1): 5-22. DOI:10.1016/j.envpol.2007.06.006 (
![](images/locate.gif)
[7] Klaine S J, Alvarez P J, Batley G E, et al. Nanomaterials in the environment: Behavior, fate, bioavailability, and effects. Environmental Toxicology and Chemistry, 2008, 27(9): 1825-1851. DOI:10.1897/08-090.1 (
![](images/locate.gif)
[8] Behra R, Krug H. Nanoecotoxicology: Nanoparticles at large. Nature Nanotechnology, 2008, 3(5): 253-254. DOI:10.1038/nnano.2008.113 (
![](images/locate.gif)
[9] Miller R J, Lenihan H S, Muller E B, et al. Impacts of metal oxide nanoparticles on marine phytoplankton. Environmental Science & Technology, 2010, 44(19): 7329-7334. DOI:10.1021/es100247x (
![](images/locate.gif)
[10] Nel A, Xia T, M?dler L, et al. Toxic potential of materials at the nanolevel. Science, 2006, 311(5761): 622-627. DOI:10.1126/science.1114397 (
![](images/locate.gif)
[11] Zhu X, Chang Y, Chen Y. Toxicity and bioaccumulation of TiO2 nanoparticle aggregates in Daphnia magna. Chemosphere, 2010, 78(3): 209-215. DOI:10.1016/j.chemosphere.2009.11.013 (
![](images/locate.gif)
[12] Yu Y, Ren W, Ren B. Nanosize titanium dioxide cause neuronal apoptosis: A potential linkage between nanoparticle exposure and neural disorder. Neurological Research, 2008, 30(10): 1115-1120. DOI:10.1179/0161641215Z.000000000587 (
![](images/locate.gif)
[13] Jugan M L, Barillet S, Simon-Deckers A, et al. Cytotoxic and genotoxic impact of TiO2 nanoparticles on A549 cells. Journal of Biomedical Nanotechnology, 2011, 7(1): 22-23. DOI:10.1166/jbn.2011.1181 (
![](images/locate.gif)
[14] Li Y, Zhang W, Niu J, et al. Mechanism of photogenerated reactive oxygen species and correlation with the antibacterial properties of engineered metal-oxide nanoparticles. ACS Nano, 2012, 6(6): 5164-5173. DOI:10.1021/nn300934k (
![](images/locate.gif)
[15] Federici G, Shaw B J, Handy R D. Toxicity of titanium dioxide nanoparticles to rainbow trout (Oncorhynchus mykiss): Gill injury, oxidative stress, and other physiological effects. Aquatic Toxicology, 2007, 84(4): 415-430. DOI:10.1016/j.aquatox.2007.07.009 (
![](images/locate.gif)
[16] Rincón A G, Pulgarin C. Bactericidal action of illuminated TiO2 on pure Escherichia coli and natural bacterial consortia: Post-irradiation events in the dark and assessment of the effective disinfection time. Applied Catalysis B: Environmental, 2004, 49(2): 99-112. DOI:10.1016/j.apcatb.2003.11.013 (
![](images/locate.gif)
[17] Holden P, Horst A, Neal A, et al. Metal and Metal Oxide Nanoparticle Interactions with Pseudomonas. Santa Barbara: University of California-Santa Barbara, 2007. (
![](images/locate.gif)
[18] Schins R P F, Duffin R, H?hr D, et al. Surface modification of quartz inhibits toxicity, particle uptake, and oxidative DNA damage in human lung epithelial cells. Chemical Research in Toxicology, 2002, 15(9): 1166-1173. DOI:10.1021/tx025558u (
![](images/locate.gif)
[19] Quik J T K, Vonk J A, Hansen S F, et al. How to assess exposure of aquatic organisms to manufactured nanoparticles?. Environment International, 2011, 37(6): 1068-1077. DOI:10.1016/j.envint.2011.01.015 (
![](images/locate.gif)
[20] Zhou D, Abdel-Fattah A I, Keller A A. Clay particles destabilize engineered nanoparticles in aqueous environments. Environmental Science & Technology, 2012, 46(14): 7520-7526. DOI:10.1021/es3004427 (
![](images/locate.gif)
[21] Oesterreich T, Klaus U, Volk M, et al. Environmental fate of amitrole: Influence of dissolved organic matter. Chemosphere, 1999, 38(2): 379-392. DOI:10.1016/S0045-6535(98)00185-4 (
![](images/locate.gif)
[22] Noblet J A, Smith L A, Suffet I H. Influence of natural dissolved organic matter, temperature, and mixing on the abiotic hydrolysis of triazine and organophosphate pesticides. Journal of Agricultural and Food Chemistry, 1996, 44(11): 3685-3693. DOI:10.1021/jf960315r (
![](images/locate.gif)
[23] Karlsson T, Persson P, Skyllberg U. Complexation of copper(II) in organic soils and in dissolved organic matter - EXAFS evidence for chelate ring structures. Environmental Science & Technology, 2006, 40(8): 2623-2628. DOI:10.1021/es052211f (
![](images/locate.gif)
[24] Hakala J A, Chin Y P, Weber E J. Influence of dissolved organic matter and Fe(II) on the abiotic reduction of pentachloronitrobenzene. Environmental Science & Technology, 2007, 41(21): 7337-7342. DOI:10.1021/es070648c (
![](images/locate.gif)
[25] Stumm W. Chemical interaction in particle separation. Environmental Science & Technology, 1977, 11(12): 1066-1070. DOI:10.1021/es60135a010 (
![](images/locate.gif)
[26] Tatzber M, Stemmer M, Spiegel H, et al. FTIR-spectroscopic characterization of humic acids and humin fractions obtained by advanced NaOH, Na4P2O7, and Na2CO3 extraction procedures. Journal of Plant Nutrition and Soil Science, 2007, 170(4): 522-529. DOI:10.1002/jpln.200622082 (
![](images/locate.gif)
[27] Leivisk? T, Nurmesniemi H, P?yki? R, et al. Effect of biological wastewater treatment on the molecular weight distribution of soluble organic compounds and on the reduction of BOD, COD and P in pulp and paper mill effluent. Water Research, 2008, 42(14): 3952-3960. DOI:10.1016/j.watres.2008.06.016 (
![](images/locate.gif)
[28] Chen J, LeBoeuf E J, Dai S, et al. Fluorescence spectroscopic studies of natural organic matter fractions. Chemosphere, 2003, 50(5): 639-647. DOI:10.1016/S0045-6535(02)00616-1 (
![](images/locate.gif)
[29] Canellas L P, Olivares F L, Aguiar N O, et al. Humic and fulvic acids as biostimulants in horticulture. Scientia Horticulturae, 2015, 196: 15-27. DOI:10.1016/j.scienta.2015.09.013 (
![](images/locate.gif)
[30] Barber L B, Leenheer J A, Noyes T I, et al. Nature and transformation of dissolved organic matter in treatment wetlands. Environmental Science & Technology, 2001, 35(24): 4805-4816. (
![](images/locate.gif)
[31] Francioso O, Sanchez-Cortes S, Tugnoli V, et al. Infrared, Raman, and nuclear magnetic resonance (1H, 13C, and 31P) spectroscopy in the study of fractions of peat humic acids. Applied Spectroscopy, 1996, 50(9): 1165-1174. DOI:10.1366/0003702963905169 (
![](images/locate.gif)
[32] Chen Y, Senesi N, Schnitzer M. Information provided on humic substances by E4/E6 ratios. Soil Science Society of America Journal, 1977, 41(2): 352-358. DOI:10.2136/sssaj1977.03615995004100020037x (
![](images/locate.gif)
[33] Thurman E M. Organic Geochemistry of Natural Waters. Dordrecht: Springer Netherlands, 1985. DOI:10.1007/978-94-009-5095-5 (
![](images/locate.gif)
[34] Greenland D J, Hayes M H B. The Chemistry of Soil Constituents. Chichester: John Wiley and Sons, 1978. DOI:10.1016/0012-8252(80)90080-X (
![](images/locate.gif)
[35] Chen J, Gu B, LeBoeuf E J, et al. Spectroscopic characterization of the structural and functional properties of natural organic matter fractions. Chemosphere, 2002, 48(1): 59-68. DOI:10.1016/S0045-6535(02)00041-3 (
![](images/locate.gif)
[36] Leenheer J A, Wilson M A, Malcolm R L. Presence and potential significance of aromatic-ketone groups in aquatic humic substances. Organic Geochemistry, 1987, 11(4): 273-280. DOI:10.1016/0146-6380(87)90038-6 (
![](images/locate.gif)
[37] Schnitzer M, Kahn S U. Humic Substances in the Environment. New York: Marcel Dekker, 1972. (
![](images/locate.gif)
[38] Her N, Amy G, McKnight D, et al. Characterization of DOM as a function of MW by fluorescence EEM and HPLC-SEC using UVA, DOC, and fluorescence detection. Water Research, 2003, 37(17): 4295-4303. DOI:10.1016/S0043-1354(03)00317-8 (
![](images/locate.gif)
[39] Coble P G. Characterization of marine and terrestrial DOM in seawater using excitation-emission matrix spectroscopy. Marine Chemistry, 1996, 51(4): 325-346. DOI:10.1016/0304-4203(95)00062-3 (
![](images/locate.gif)
[40] Senesi N. Molecular and quantitative aspects of the chemistry of fulvic acid and its interactions with metal ions and organic chemicals: Part Ⅱ. The fluorescence spectroscopy approach. Analytica Chimica Acta, 1990, 232: 77-106. DOI: 10.1016/S0003-2670(00)81226-X. (
![](images/locate.gif)
[41] Mobed J J, Hemmingsen S L, Autry J L, et al. Fluorescence characterization of IHSS humic substances: Total luminescence spectra with absorbance correction. Environmental Science & Technology, 1996, 30(10): 3061-3065. DOI:10.1021/es960132l (
![](images/locate.gif)
[42] Miano T M, Senesi N. Synchronous excitation fluorescence spectroscopy applied to soil humic substances chemistry. Science of The Total Environment, 1992, 117-118: 41-51. DOI:10.1016/0048-9697(92)90071-Y (
![](images/locate.gif)
[43] Gu B, Schmitt J, Chen Z, et al. Adsorption and desorption of natural organic matter on iron oxide: Mechanisms and models. Environmental Science & Technology, 1994, 28(1): 38-46. DOI:10.1021/es00050a007 (
![](images/locate.gif)
[44] Davis W M, Erickson C L, Johnston C T, et al. Quantitative Fourier Transform Infrared spectroscopic investigation humic substance functional group composition. Chemosphere, 1999, 38(12): 2913-2928. DOI:10.1016/S0045-6535(98)00486-X (
![](images/locate.gif)
[45] Manciulea A, Baker A, Lead J R. A fluorescence quenching study of the interaction of Suwannee River fulvic acid with iron oxide nanoparticles. Chemosphere, 2009, 76(8): 1023-1027. DOI:10.1016/j.chemosphere.2009.04.067 (
![](images/locate.gif)