Author NameAffiliation
Xiaoyu ChenSchool of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
School of Electromechanic Engineering, Qingdao University, Qingdao 266071, Shandong, China
Hongze FangSchool of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
Qi WangSchool of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
Ruirun ChenSchool of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
Hongsheng DingSchool of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
Yanqing SuSchool of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
Jingjie GuoSchool of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
Abstract:
In order to refine microstructure grains and improve mechanical properties of TiAl alloys, Ti44Al (at.%) alloy was rapidly solidified by melt spinning under different cooling rates. Microstructure and microhardness of the alloy before and after rapid solidification were investigated. XRD results show that the ratio of α2 phase in binary alloy increased with the cooling rates, which is caused by more α phases directly transforming to α2 phases. Grain morphology changed from long dendrite to the mixture of equiaxed and dendrite to equiaxed with the increase of cooling rates. The grain size was refined from 200-600 μm of as-cast to 18 μm of the alloy cooled at 4.9×105K/s, which is caused by the undercooling induced from rapid solidification. Lamellar spacing was decreased from 4.5 μm of as-cast to 1.1 μm by rapid solidification. With the increase of cooling rate, the content of α 2 phase increased and γ phase decreased gradually. Rapid solidification can reduce the segregation of elements. The microhardness was improved from 247 HV to 556 HV, which results from grain refinement strengthening, reduction of lamellar spacing, and more content of α2 phase.
Key words:Ti-44Al alloymicrostructuremicrohardnessmelt spinningsolidification path
DOI：10.11916/j.issn.1005-9113.20042
CLC NUMBER:TG146
Fund:
Xiaoyu Chen, Hongze Fang, Qi Wang, Ruirun Chen, Hongsheng Ding, Yanqing Su, Jingjie Guo. Effects of Rapid Cooling Rate on Microstructure Formation and Microhardness of Binary Ti-44Al Alloy[J]. Journal of Harbin Institute of Technology (New Series), 2020, 27(3): 225-232. DOI: 10.11916/j.issn.1005-9113.20042
Fund Sponsored by the National Natural Science Foundation of China (Grant No. 51825401) and the China Postdoctoral Science Foundation (Grant No. 2019TQ0077) Corresponding author Ruirun Chen, Winner of the National Science Fund for Distinguished Young Scholars. E-mail: ruirunchen@hit.edu.cn Article history Received: 2020-05-05
ContentsAbstractFull textFigures/TablesPDF
Effects of Rapid Cooling Rate on Microstructure Formation and Microhardness of Binary Ti-44Al Alloy
Xiaoyu Chen1,2, Hongze Fang1, Qi Wang1, Ruirun Chen1
, Hongsheng Ding1, Yanqing Su1, Jingjie Guo1 1. School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China;
2. School of Electromechanic Engineering, Qingdao University, Qingdao 266071, Shandong, China
Received: 2020-05-05
Sponsored by the National Natural Science Foundation of China (Grant No. 51825401) and the China Postdoctoral Science Foundation (Grant No. 2019TQ0077)
Ruirun Chen is a professor, doctoral supervisor, and the Vice Director at the Interdisciplinary Research Center at Harbin Institute of Technology, Winner of the National Science Fund for Distinguished Young Scholars.His primary research interests are solidification theory and casting process of advanced materials, including titanium-aluminum alloy, niobium-silicon alloy, high-entropy alloy, metal-based hydrogen storage material, solar-grade silicon, and so on.
Corresponding author: Ruirun Chen, Winner of the National Science Fund for Distinguished Young Scholars. E-mail: ruirunchen@hit.edu.cn.
Abstract: In order to refine microstructure grains and improve mechanical properties of TiAl alloys, Ti44Al (at.%) alloy was rapidly solidified by melt spinning under different cooling rates. Microstructure and microhardness of the alloy before and after rapid solidification were investigated. XRD results show that the ratio of α2 phase in binary alloy increased with the cooling rates, which is caused by more α phases directly transforming to α2 phases. Grain morphology changed from long dendrite to the mixture of equiaxed and dendrite to equiaxed with the increase of cooling rates. The grain size was refined from 200-600 μ m of as-cast to 18 μ m of the alloy cooled at 4.9×105K/s, which is caused by the undercooling induced from rapid solidification. Lamellar spacing was decreased from 4.5 μ m of as-cast to 1.1 μ m by rapid solidification. With the increase of cooling rate, the content of α2 phase increased and γ phase decreased gradually. Rapid solidification can reduce the segregation of elements. The microhardness was improved from 247 HV to 556 HV, which results from grain refinement strengthening, reduction of lamellar spacing, and more content of α2 phase.
Keywords: Ti-44Al alloymicrostructuremicrohardnessmelt spinningsolidification path
1 Introduction TiAl-based alloys have been applied in aviation and astronautics, military, vehicle engineering, and biomedical engineering, due to their low density, high intensity, good creep resistance, and excellent properties at high temperature[1-5]. However, the as-cast microstructures are coarse columnar lamellar (α2+ γ) grains which produce low fracture toughness and poor room-temperature ductility[6-7]. Improving the ductility of TiAl-based alloys has recently been a focus of research. It is suggested that rapid solidification is an important branch in the field of materials science and engineering, which generates smaller grains, homogenous microstructures, and more excellent properties than conventional solidification[8-10]. The microstructures, the primary phase, and the microhardness of rapid solidified TiAl alloys can also be changed with increasing undercooling[11-13].
The microstructures of binary TiAl alloys are controlled by the volume fraction of α2/γ. According to thermodynamic equilibrium theory, the volume fractions of α2/γ of binary alloys are mainly affected by the content of aluminum[14-16]. Kenel and Leinenbach[17] used the CALPHAD approach to predict and explain the microstructure of binary TiAl alloys under high cooling rates. They found that when Al ≤ 45 at.%, the alloys formed a coarse-grained α/α2 microstructure, while the alloys showed mixed microstructure consisting of coarse α/α2 grains when 45 < Al < 48 at.% with local gamma grains and lamellar α2 + γ. Ti-48Al alloy exhibits dendritic microstructure of lamellar α2 + γ dendrites and interdendritic gamma grains. L et al.[18] concluded that the two-phase (α and γ) coupled growing morphology in Ti-(51-54) Al (at.%) changes from regular lamellar to irregular blocks and equiaxed structures with the decrease of temperature gradient during growth. The solute diffusion and the dissolution of γ phase play important roles in coupled microstructure evolution. The transformation from a peritectic (L+α→γ) to metastable eutectic reaction (L→α+γ) of TiAl alloys induces the formation of two-phase coupled growth morphologies[19]. Actually, the study about binary TiAl alloys via rapid solidification is expected to be further studied and improved.
Chill-block melt-spinning method is frequency used to prepare TiAl-based alloys ribbons[20-21] with a flat surface and a thin thickness. Images captured by high speed infrared imaging revealed that ribbon formation is controlled by thermal transfer[22]. Most of the cooling rates are calculated by counting the rate of heat flow in Newton′s cooling mode[23-24]. The roll wheel speed and the cooling rate are in linear correlation, and the cooling rate increases with the increase of roll wheel speed.
Controlling microstructure of TiAl-based alloys strongly depends on both Al concentration and cooling rates. In this paper, the chill-block melting-spinning method was used to prepare the binary TiAl alloy. Its phases, microstructures and mechanical properties were analyzed. Based on these data, the microstructure and its effect on mechanical properties of rapidly solidified Ti-44Al alloy were elucidated.
2 Materials and Experimental Methods As-cast ingot with nominal composition of Ti-44Al (at.%) was prepared from titanium sponge (>99.9 %, wt. %) and aluminum (> 99.9 %, wt. %) using vacuum consumable arc-melting. The samples were cut into smaller pieces for melt spinning technique. In this experiment, the wheel material was pure copper and was set at different speeds. Table 1 shows the physical parameters of alloys for calculating cooling rates. The cooling rates were calculated by Newton heat transfer model[25] in the interface, as shown by Eq.(1). The physical parameters used in Eq. (1) are listed in Table 1, and the calculated results are listed in Table 2.
表 1
Table 1 Physical parameters of Ti-44Al alloy Alloy(at.%) TA(K) T(K) h (W/m2K) cP (J/kg·K) ρ(kg/m3) d(μm) Ti-44Al 293 1 840 105 799 3 751 105.2-153.4
Table 1 Physical parameters of Ti-44Al alloy
表 2
Table 2 Cooling rates (CR) of rapidly solidified Ti-44Al alloy Samples 1 2 3 4 5 CR (K/s) 2.5×105 3.1×105 3.5×105 4.2×105 4.9×105
Table 2 Cooling rates (CR) of rapidly solidified Ti-44Al alloy
$\mathop {(\frac{{{\rm{d}}T}}{{{\rm{d}}t}})}\nolimits_{t = 0} = - \frac{h}{{\rho {c_p}d}}(T - {T_A})$ (1)
where Q is the heat transfer in the direction of heat flow, h is the heat transfer coefficient, A is the boundary area of heat flow, T is the temperature of alloy droplet, TA is the temperature of copper roll, ρ is the density of alloy, cP is the specific heat capacity, and d is the thickness of the thin strip produced by vacuum belt rejection.
The rapidly solidified specimens were polished and etched with the reagent of 5%HF+5%HNO3+90%H2O (volume fraction). Phase constitution and crystal structure were analyzed by X-ray diffraction (XRD). Microstructures were observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM, Tecnai G2 F30), compositions were measured by energy dispersive X-ray spectrometry (EDS), and microhardness was tested by HVS-1000 Digital Microhardness Tester.
3 Results and Discussion 3.1 Microstructures of As-Cast Ti-44Al Alloy Based on binary TiAl alloy phase diagram, the transformation of Ti-44Al alloy follows L→L+β→β→β+α→α→α+γ→α2+γ, as shown in Fig. 1.
Fig.1
Fig.1 Equilibrium solidification diagram of Ti-Al alloys TiAl alloys with Al ≤ 45 at.% were fully solidified via β-Ti region, while the peritectic reaction occurred when Al is 48 at.%. Figs. 2(a)-(b) show the coarse lamellae microstructure of as-cast Ti-44Al alloy. The grain sizes of this alloy are hundreds of micros (200-600 μm), and the grain boundaries are irregular. The average lamellar spacing was measured by intercept method, which was calculated as 4.5 μm. XRD results show this alloy consists of α2 and γ phases, as shown in Fig. 3.
Fig.2
Fig.2 Microstructure of as-cast Ti-44Al alloy(a) Low magnification (b) High magnification Fig.3
Fig.3 XRD pattern ofas-cast Ti-44Al alloy 3.2 Microstructure of Rapidly Solidified Ti-44Al Alloy SEM-BSE microstructures of rapidly solidified Ti-44Al alloy at different cooling rates are shown in Fig. 4. Dendrite morphologies are presented in Figs. 4(a)-(b). It is noteworthy that the primary dendrites in Fig. 4(a) are larger and longer than that in Fig. 4(b). Equiaxed grains and one dendrite are displayed in Fig. 4(c), while there are only equiaxed grains in Figs. 4(d)-(e). It can be seen that the grain morphology changes from dendrite to mixture of equiaxed grains and dendrite to equiaxed grains with the increase of cooling rates. Meanwhile, the grain size is decreased from 50 μm (cooled at 2.5×105 K/s) to 18 μm (cooled at 4.9×105K/s), the statistical results and changing trend of which are shown in Fig. 5. It can be concluded that rapid solidification not only influences grain morphology, but also grain size. When the cooling rate is low (less than 3.1×105 K/s), which means the roll rotation speed is low, the rapidly solidified alloy shows dendrite or near dendrite. Under this condition, the heat transfer is comparatively slow, which provides enough time for dendrite to be formed, as shown in Figs. 4(a)-(b). With the increase of cooling rates, dendrite morphology decreases and equiaxed grain begins to form. When cooling rate is further increased, the equiaxed grain size decreases. The discontinuous arms are caused by the supercooled liquid surrounding the first solidified alloy, which stops most of the latent heat generated from crystallization from being transmitted. Because of the high concentration of solute and low melting point at the junction of dendrite arms, the latent heat from crystallization is released here and the temperature at the junction of dendrite arms is increased. As a result, the dendrite arms are partly melted, and then become isolated and interrupted.
Fig.4
Fig.4 Microstructure of rapid solidified Ti-44Al alloy under different cooling rates (a) 2.5×105 K/s (b) 3.1×105 K/s (c) 3.5×105 K/s (d) 4.2×105 K/s (e) 4.9×105 K/s Fig.5
Fig.5 Effect of cooling rates on different average grain sizes of Ti-44Al alloy Figs. 4(c)-(e) show irregular equiaxed grains. With the increase of cooling rate, the grain size gradually decreases to about 18 μm. When the cooling rate is 3.5×105 K/s, the alloy begins to form ribbon, and the microstructure consists of equiaxed dendrites and irregular equiaxed grains (Fig. 4(c)), which is the critical state of transformation from the dendrite to the equiaxed. When the cooling rate is 4.2×105 K/s, the microstructure consists solely of irregular equiaxed grains with obvious lamellae and several light dark structures distributed around grain boundaries, as shown in Fig. 4(d). When the cooling rate is 4.9×105 K/s, there is no irregular equiaxed grain boundary, and the light dark structure becomes thinner and presents continuous network distribution. Based on the lamellar microstructure of Ti-44Al alloy and the X-ray diffraction pattern, it is considered that the gray matrix phase obtained by rapid solidification is composed of γ phase and α2 phase.
From Fig. 5, with the increase of cooling rates, the grain size of Ti-44Al alloy decreases gradually. Supercooling has an effect on nucleation rate and growth rate. Increasing supercooling in a certain range will increase the nucleation rate and growth rate at differentrates of increase. The rate of increase of nucleation rate is faster than that of growth rate, as shown in Fig. 6. In the supercooling range of general metals, the larger the undercooling degree is, the larger the ratio of nucleation rate to growth rate is, and the smaller the grain size is. In this study, the method of increasing supercooling is to increase the cooling rate of liquid metal, which changes in the order of 105 K/s. Rapid solidification technology is an efficient method to obtain fine grains. In addition, the rapid solidification at a higher cooling rate of more than 105 K/s can rapidly cool the molten liquid metal and obtain great degree of supercooling. The atoms have no time to diffuse to maintain the short-range ordered arrangement of the liquid, and to solidify to obtain the solid metal, which is the amorphous metal.
Fig.6
Fig.6 Effect of undercooling on nucleation rate and growth rate 3.3 Lamellar Structure of Rapidly Solidified Ti-44Al Alloy Lamellar structure is a very important aspect for TiAl alloys. Not only lamellar colony size, but also lamellar spacing influences their mechanical properties. Lamellar structure with higher magnification is shown in Fig. 7. Lamellar spacing was measured and the average lamellar spacing was calculated. The results are shown in Fig. 8. Lamellar spacing is decreased from 4.5 μm of as-cast to 1.1 μm of rapidly solidified at 4.9×105 K/s. It can be seen that rapid solidification can decrease the lamellar spacing, and lamellar spacing decrease with the increase of cooling rates.
Fig.7
Fig.7 Lamellae structure of rapidly solidified alloy at different cooling rates (a) 2.5×105 K/s (b) 3.1×105K/s (c) 3.5×105 K/s (d) 4.2×105 K/s (e) 4.9×105 K/s Fig.8
Fig.8 Lamellae spacing of rapidly solidified alloy at different cooling rates 3.4 Phase Composition of Rapidly Solidified Ti-44Al Alloy The rapidly solidified Ti-44Al alloy samples were examined by XRD. Results show that the phases are mainly composed of α2 phase and γ phase, as shown in Fig. 9. Main diffraction peak of α2 phase is (103) in rapid solidified Ti-44Al alloy. With the increase of cooling rate, the diffraction peaks (113) (311) of γ phase gradually decrease and disappear, which indicates the content of γ phase decreases gradually, whereas α2 phase increases. The volume fraction of γ phase is lower than that of as-cast alloy. Phase volume fraction of as-cast and rapidly solidified Ti-44Al alloy with different cooling rates is listed in Table 3.
Fig.9
Fig.9 XRD patterns of rapidly solidified Ti-44Al alloy 表 3
Table 3 Phase volume fraction of as-cast and rapidly solidified Ti-44Al alloy Cooling rate(K/s) α2 phase (%) γ phase (%) As-cast 38.7 61.3
2.5×105 45.6 54.4
3.1×105 48.8 51.2
3.5×105 50.2 49.8
4.2×105 53.1 46.9
4.2×105 54.7 45.3
Table 3 Phase volume fraction of as-cast and rapidly solidified Ti-44Al alloy
The microstructure of rapidly solidified Ti-44Al alloy was analyzed by TEM, as shown in Fig. 10. The matrix is massive α2 phase, and the lathy shape is γ phase. The lamellae structures are observed in other regions and the coarse lamellae are broken down into smaller lamellar. The formation of lamellar is incomplete. Based on the structural characteristics of the Ti-44Al alloy before and after rapid solidification, the primary phase of as-cast Ti-44Al alloy is β phase, while it is α phase when it is rapidly solidified. With increasing cooling rate, the stable primary β phase was depressed, and the (L+α) metastable zone of undercooled alloys firstly solidified. Most of metastable α phase was reserved, and then orderly transformed into α2 phase instead of completely changing into γ phase. The γ phase in lathy shape always nucleates and grows at the grain boundary and some high energy areas, such as stacking fault. In addition, the lamellar structure forms incompletely, resulting from slower diffusion of elements. The higher the cooling rate is, the less time the elements diffuse. Based on the above analysis, solidification path of rapidly solidified Ti-44Al alloy is L→L+α→α+γm→ α+α2+γm →(α2+γ) +α2+γm→α2+γ+γm.
Fig.10
Fig.10 TEM images of rapidly solidified TiAl alloy at 4.9×105 K/s (a) α2 and γ phase (b-c) α2 and γ lamellar (d)SAED pattern of α2 and γ lamellar 3.5 Compositional Distribution of Rapidly Solidified Ti-44Al Alloy Besides refining the grain size of the alloy, rapid solidification can reduce the segregation of elements. Energy spectrum analysis was carried out at different areas including bright contrast area (I), dark contrast area (II), and grain boundary (III), as shown in Fig. 4. The analyses results are shown in Table 4. When the cooling rate is 2.5×105 K/s, the Al content of all areas are 47.30 at.%, 47.24 at.%, and 46.92 at.%, respectively, which are all more than 44 at.%. When the cooling rate is 3.1×105 K/s, the Al content of bright contrast area is 42.65 at.%, which is less than 44 at.%, but those of other two areas are a little higher than normal. When the cooling rate increases to 3.5×105 K/s, the contents of Al are 46.03 at. %, 45.22 at.%, and 45.28 at.%, respectively, which are close to 44 at.%. The above EDS data show that there is a segregation of Al element when the cooling rate is low. At a higher cooling rate, the Al content of the three areas are 44.35 at.%, 43.82 at.%, and 44.52 at.%, respectively, where the segregation is very little.
表 4
Table 4 EDS results of different areas of the rapidly solidified Ti-44Al alloy Cooling rate(K/s)Bright contrast area (Ⅰ)Bright contrast area (Ⅱ)Bright contrast area (Ⅲ) Al (at.%) Ti (at.%) Al (at.%) Ti (at.%) Al (at.%) Ti (at.%)
2.5×105 47.30 52.70 47.24 52.76 46.92 53.08
3.1×105 42.65 57.35 45.76 54.24 45.83 54.17
3.5×105 46.03 53.97 45.22 54.78 45.28 54.72
4.2×105 43.26 56.74 44.14 55.86 44.61 55.39
4.9×105 44.35 55.65 43.82 56.18 44.52 55.48
Table 4 EDS results of different areas of the rapidly solidified Ti-44Al alloy
3.6 Microhardness of As-Cast and Rapidly Solidified Ti-44Al Alloy Fig. 11 shows the microhardness of as-cast and rapidly solidified Ti-44Al alloy. It is noted that the microhardness of all rapidly solidified alloy is improved more than 100 %, which increases with increasing cooling rates. When the cooling rate is 4.9×105K/s, the microhardness reaches 556 HV. The improvement of microhardness results from grain refinement strengthening, reduction of lamellar spacing, and the variation of phase proportions. It is confirmed that β phase is the hardest in TiAl-based alloys, α2 phase is intermediate, and γ phase is the weakest of all. According to the above conclusion, the volume fraction of α2 phase increases in rapidly solidified Ti-44Al alloy. Consequently, it is meaningful to improve the mechanical properties of TiAl-based alloys by controlling the α2/γ ratio except during refining.
Fig.11
Fig.11 Microhardness of as-cast and rapidly solidified Ti-44Al alloy 4 Conclusions 1) Grain morphology changes from long dendrite to the mixture of equiaxed grains and dendrite to equiaxed grains with the increase of cooling rates. The grain size was refined as 50 μm (cooled at 2.5×105 K/s) and 18 μm (cooled at 4.9×105 K/s) from hundreds of micros (200-600 μm) as-cast. They result from undercooling induced by rapid solidification.
2) The phases are mainly composed of α2 phase and γ phase. With the increase of cooling rate, the content of α2 phase increased and γ phase decreased gradually. The volume fraction of γ phase was lower than that of as-cast alloy.
3) Lamellar spacing was decreased from 4.5 μm of as-cast to 1.1 μm of rapidly solidified at 4.9×105 K/s. Rapid solidification can reduce the segregation of elements. The faster the solidification rate, the more uniform the composition.
4) The microhardness of rapidly solidified Ti-44Al alloy were greatly improved, which was increased from 247 HV to 556 HV. The improvement of the microhardness results from grain refinement strengthening, reduction of lamellar spacing, and more α2 phase.
References
[1] Wei D X, Koizumi Y, Nagasako M, et al. Refinement of lamellar structures in Ti-Al alloy. Acta Materialia, 2017, 125: 81-97. DOI:10.1016/j.actamat.2016.11.045 (
0)[2] Wang Q, Chen R R, Yang Y H, et al. High-throughput analysis of Al and Nb effects on mechanical behaviour of TiAl alloys using electromagnetic cold crucible continuous casting. Journal of Alloys and Compounds, 2019, 775: 124-131. DOI:10.1016/j.jallcom.2018.10.097 (
0)[3] Wu Y L, Hu R, Yang J R, et al. In-situ observation of microstructure evolution and phase transformation under continuous cooling in Ru-containing TiAl alloys. Materials Characterization, 2020, 163: 110296. DOI:10.1016/j.matchar.2020.110296 (
0)[4] Castillo-Rodriguez M, Nó M L, Jimenez J A, et al. High temperature internal friction in a Ti-46Al-1Mo-0.2Si intermetallic, comparison with creep behavior. . Acta Materialia, 2016, 103: 46-56. DOI:10.1016/j.actamat.2015.09.052 (
0)[5] Chen R R, Fang H Z, Chen X Y, et al. Formation of TiC/Ti2AlC and α2+γ in in-situ TiAl composites with different solidification paths. Intermetallics, 2017, 81: 9-15. DOI:10.1016/j.intermet.2017.02.025 (
0)[6] Ohnuma I, Fujita Y, Mitsui H, et al. Phase equilibria in the Ti-Al binary system. Acta Materialia, 2000, 48(12): 3113-3123. DOI:10.1016/S1359-6454(00)00118-X (
0)[7] Zhang K, Hu R, Lei T C, et al. Refinement of massive γ phase with enhanced properties in a Ta containing γ-TiAl-based alloys. Scripta Materialia, 2019, 1720: 113-118. DOI:10.1016/j.scriptamat.2019.06.035 (
0)[8] Sokolovsky V S, Stepanov N D, Zherebtsov S V, et al. The effect of Gd addition on the kinetics of α2→γ transformation in γ-TiAl based alloys. Intermetallics, 2020, 120: 106759. DOI:10.1016/j.intermet.2020.106759 (
0)[9] Kenel C, Leinenbach C. Influence of Nb and Mo on microstructure formation of rapidly solidified ternary TieAl-(Nb, Mo) alloys. Intermetallics, 2016, 69: 82-89. DOI:10.1016/j.intermet.2015.10.018 (
0)[10] Chen R R, Wang Q, Zhou Z C, et al. Microstructure tensile properties and creep behavior of high-Al TiAlNb alloy using electromagnetic cold crucible continuous casting. Journal of Alloys and Compounds, 2019, 801: 166-174. DOI:10.1016/j.jallcom.2019.06.111 (
0)[11] Luo Z C, Wang H P. Primary dendrite growth kinetics and rapid solidification mechanism of highly undercooled Ti-Al alloys. Journal of Materials Science & Technology, 2020, 40: 47-53. DOI:10.1016/j.jmst.2019.08.034 (
0)[12] Liang C, Zhao J F, Chang J, et al. Microstructure evolution and nano-hardness modulation of rapidly solidified Ti-Al-Nb alloy. Journal of Alloys and Compounds, 2020, 836: 155538. DOI:10.1016/j.jallcom.2020.155538 (
0)[13] Kastenhuber M, Klein T, Rashkova B, et al. Phase transformations in a β-solidifyingγ-TiAl based alloy during rapid solidification. Intermetallics, 2017, 91: 100-109. DOI:10.1016/j.intermet.2017.08.017 (
0)[14] Wei D X, Koizumi Y, Li Y P, et al. Submicron lamellar porous structure formed by selective dissolution of Ti-Al alloy. Materials and Design, 2016, 98: 1-11. DOI:10.1016/j.matdes.2016.02.096 (
0)[15] Kan W, Chen B, Peng H, et al. Formation of columnar lamellar colony grain structure in a high Nb-TiAl alloy by electron beam melting. Journal of Alloys and Compounds, 2019, 809: 151673. DOI:10.1016/j.jallcom.2019.151673 (
0)[16] Schuster J C, Palm M. Reassessment of the binary Aluminum-Titanium phase diagram. Journal of Phase Equilibria and Diffusion, 2006, 27: 255-277. DOI:10.1361/154770306X109809 (
0)[17] Kenel C, Leinenbach C. Influence of cooling rate on microstructure formation during rapid solidification of binary TiAl alloys. Journal of Alloys and Compounds, 2015, 637: 242-247. DOI:10.1016/j.jallcom.2015.03.016 (
0)[18] Liu Y C, Yang G C, Guo X F, et al. Coupled growth behavior in the rapidly solidified Ti-Al peritectic alloys. Journal of Crystal Growth, 2001, 222(3): 645-654. DOI:10.1016/S0022-0248(00)00946-5 (
0)[19] Kim W T, Cantor B. The variation of grain size with cooling rate during melt spinning. Scripta Metallurgica etMaterialia, 1990, 24(4): 633-637. DOI:10.1016/0956-716X(90)90214-2 (
0)[20] Jones H. Cooling rates during rapid solidification from a chill surface. Materials Letters, 1996, 26(3): 133-136. DOI:10.1016/0167-577X(95)00213-8 (
0)[21] ?ad?rl? E, Kaya H, Gündüz M. Effect of growth rates and temperature gradients on the lamellar spacing and the undercooling in the directionally solidified Pb-Cd eutectic alloy. Materials Research Bulletin, 2003, 38(9-10): 1457-1476. DOI:10.1016/S0025-5408(03)00169-7 (
0)[22] Nagashio K, Kuribayashi K. Experimental verification of ribbon formation processin chill-block melt spinning. Acta Materialia, 2006, 54(9): 2353-2360. DOI:10.1016/j.actamat.2006.01.025 (
0)[23] Lavernia E J, Srivatsan T S. The rapid solidification processing of materials: science, principles, technology, advances, and applications. Journal of Materials Science, 2010, 45: 287-325. DOI:10.1007/s10853-009-3995-5 (
0)[24] Liu Z G, Chai L H, Chen Y Y. Effect of cooling rate and Y element on the microstructure of rapidly solidified TiAl alloys. Journal of Alloys and Compounds, 2010, 504(S1): S491-S495. DOI:10.1016/j.jallcom.2010.02.054 (
0)[25] Kenel C, Grolimund D, Fife J L, et al. Combined in situ synchrotron micro X-ray diffraction and high-speed imaging on rapidly heated and solidified Ti-48Al under additive manufacturing conditions. Scripta Materialia, 2016, 114: 117-120. DOI:10.1016/j.scriptamat.2015.12.009 (
0)