1.
Introduction
Gallium oxide (Ga2O3) has recently attracted attention from the science community due to its interesting properties such as good thermal stability, high dielectric constant, and wide bandgap[1]. Ga2O3 has five polymorphs: α, β, γ, δ, and ε[2]. Of its many forms, β-Ga2O3 receives the most attention from researchers because it is the most stable form of Ga2O3. β-Ga2O3 has been reported for making devices such as light-emitting diodes[3], ultraviolet (UV) detectors[4, 5], transparent electrode for deep-UV devices[6, 7], metal-oxide-semiconductor field-effect transistors (FET)[8], and high dielectric oxide materials for FET devices[9, 10]. Various growth techniques, such as molecular beam epitaxy (MBE)[11, 12], pulsed laser deposition (PLD)[6, 10, 13], sputtering[14, 15], chemical vapor deposition[16], sol–gel method[4], and hydride vapor phase epitaxy[17] have been explored to obtain β-Ga2O3 films. Among these methods, PLD shows several advantages due to completely compositional consistency from a target to the deposited film and it is suitable for low temperature growth of thin films.
We have systematically investigated the substrate temperature effect on the structural and optical properties of the β-Ga2O3 films on a (0001) sapphire substrate grown by PLD and revealed that (
![](http://www.jos.ac.cn/article/id/18070026_Z-20190109065240-1.png)
2.
Experiment
Gallium oxide films were grown on a (0001) sapphire substrate with a homemade oxygen plasma-assisted PLD system which has a growth chamber, an oxygen plasma source and a KrF excimer laser (λ = 248 nm) with a frequency of 2 Hz and energy of 225 mJ/cm2. The oxygen plasma cell was surrounded by a helical RF (13.56 MHz) coil. The sapphire substrate was ultrasonically cleaned in methanol for 20 min and again in acetone for 20 min. Then, the substrate was etched in a hot acidic solution H3PO4 : H2SO4 (1 : 3) for 5 min to remove residual oxides on the surface. Finally, it was rinsed with deionized water and followed by N2 blow drying before the substrate was introduced into the growth chamber. Facing the substrate, a 99.99% pure Ga2O3 ceramic disk was set as the target. Prior to deposition, the growth chamber was evacuated to pressure below 5 × 10?6 Pa with a turbo molecular pump. High purity oxygen gas (99.999%) was then introduced into the oxygen plasma cell through a mass flow controller. The oxygen pressure used in this work was kept at 0.01 Pa and substrate temperature was kept at 500 °C while applied RF power was varied from 0 to 300 W. The growth time was 180 min for all samples.
After growth, the thickness of the films were determined by a step profile analyzer. The structural properties of the films were characterized by X-ray diffraction (XRD) (Cu anode, Kα line, λ = 1.54 ?). Raman measurements were performed on a Horiba Jobin Yvon LabRAM HR 800 system with an Ar laser operating at a wavelength of 488 nm as the excitation source at room temperature. Optical transmittance spectra were measured by a UV-vis spectrophotometer. Surface morphology and roughness of the films were determined by an atomic force microscope (AFM).
3.
Results and discussion
Fig. 1 shows the dependence of film growth rate for β-Ga2O3 on RF power at 500 °C. Film grown in plasma generated oxygen radical background shows significant increase in growth rate compared to film grown in non-reactive O2 ambient. The growth rate of film in oxygen radical background was 2.7 times faster than film grown in non-reactive oxygen ambient (at 0.01 Pa). The 100 and 200 W samples had similar growth rate of 105 and 104 nm/h, respectively and the 300 W sample grew only slightly faster at 113 nm/h. In other words, increasing RF power of the plasma source made a small increase to film growth rate.
![](http://www.jos.ac.cn/fileBDTXB/journal/article/jos/2019/12/PIC/18070026-1_mini.jpg)
class="figure_img" id="Figure1"/>
Download
![](http://www.jos.ac.cn:80//style/web/images/down-img.png)
Larger image
![](http://www.jos.ac.cn:80//style/web/images/down-ppt.png)
PowerPoint slide
Figure1.
Dependence of growth rate of film on plasma RF power ranged from 0 to 300 W at substrate temperature of 500 °C.
XRD patterns of θ–2θ scan for the samples fabricated with different RF power are shown in Fig. 2. All samples showed diffraction peaks at 18.9°, 38.2°, 58.9°, and 82.0° and by comparing these peaks to data in the International Center for Diffraction Data catalog, these peaks correspond to (
![](http://www.jos.ac.cn/article/id/18070026_Z-20190109065357-2.png)
![](http://www.jos.ac.cn/article/id/18070026_Z-20190109065408-3.png)
![](http://www.jos.ac.cn/article/id/18070026_Z-20190109065419-4.png)
![](http://www.jos.ac.cn/article/id/18070026_Z-20190109065430-5.png)
![](http://www.jos.ac.cn/fileBDTXB/journal/article/jos/2019/12/PIC/18070026-2_mini.jpg)
class="figure_img" id="Figure2"/>
Download
![](http://www.jos.ac.cn:80//style/web/images/down-img.png)
Larger image
![](http://www.jos.ac.cn:80//style/web/images/down-ppt.png)
PowerPoint slide
Figure2.
XRD 2θ/θ scan for films fabricated at 500 °C and RF power ranged from 0 to 300 W.
Raman spectra, shown in Fig. 3, are obtained at room temperature for β-Ga2O3 films fabricated at different RF power to confirm the crystal structure. Raman spectroscopy identifies vibrational mode in a crystal structure. Raman shift peaks were identified for all samples ranging from 100 to 1000 cm?1. For the 100 W sample, peaks were observed at 144, 167, 198.5, 350.4, 470, 652.6, and 767.8 cm?1 and assigned to phonon mode of Bg(2), Ag(2), Ag(3), Ag(5)/Bg(3), Ag(7)/Bg(4), Ag(9)/Bg(5), and Ag(10), respectively by comparing these peaks to the data of bulk monoclinic β-Ga2O3[25]. Similarly, peaks of all samples and their respective phonon modes are summarized in Table 1. The results in Table 1 were consistent with the XRD analysis that all samples discussed above were monoclinic β-Ga2O3. It is noted that several peaks are not observed in the 0 W sample. This is probably because the intensity of peak observed for 0 W sample was much weaker than intensity of other samples and weak peaks cannot differentiate itself from the noise. This could be a result of insufficient thickness or deterioration in crystal quality.
![](http://www.jos.ac.cn/fileBDTXB/journal/article/jos/2019/12/PIC/18070026-3_mini.jpg)
class="figure_img" id="Figure3"/>
Download
![](http://www.jos.ac.cn:80//style/web/images/down-img.png)
Larger image
![](http://www.jos.ac.cn:80//style/web/images/down-ppt.png)
PowerPoint slide
Figure3.
Raman scattering spectra of samples prepared at substrate temperature of 500 °C and power ranged from 0 to 300 W.
Peak location (cm?1) | Phonon mode | ||||
0 W | 100 W | 200 W | 300 W | Bulk | |
– | 144 | 143.4 | 142.1 | 147 | Bg(2) |
– | 167 | 167 | 166.4 | 169 | Ag(2) |
198.5 | 198.5 | 198.5 | 198.5 | 199 | Ag(3) |
– | 348.3 | 345.2 | 344.6 | 346/353 | Ag(5)/Bg(3) |
– | 470.7 | – | – | 475/475 | Ag(7)/Bg(4) |
652.6 | 652.6 | 652.6 | 652.6 | 651/657 | Bg(5)/Ag(9) |
– | 767.8 | 768.4 | 763 | 763 | Ag(10) |
Table1.
Phonon modes for different samples compared with bulk β-Ga2O3.
Table options
-->
![](http://www.jos.ac.cn:80//style/web/images/down-csv.png)
Download as CSV
Peak location (cm?1) | Phonon mode | ||||
0 W | 100 W | 200 W | 300 W | Bulk | |
– | 144 | 143.4 | 142.1 | 147 | Bg(2) |
– | 167 | 167 | 166.4 | 169 | Ag(2) |
198.5 | 198.5 | 198.5 | 198.5 | 199 | Ag(3) |
– | 348.3 | 345.2 | 344.6 | 346/353 | Ag(5)/Bg(3) |
– | 470.7 | – | – | 475/475 | Ag(7)/Bg(4) |
652.6 | 652.6 | 652.6 | 652.6 | 651/657 | Bg(5)/Ag(9) |
– | 767.8 | 768.4 | 763 | 763 | Ag(10) |
The transmittances of the films, shown in Fig. 4, were above 80% in the visible and UV regions and sharp absorption edges were observed around wavelength of 250 nm for all the films grown in ambient oxygen radical. In addition, absorption edge of the samples with plasma treatment are steeper than the adsorption edge of the sample without plasma treatment but this is because the thickness of the films are not the same.
![](http://www.jos.ac.cn/fileBDTXB/journal/article/jos/2019/12/PIC/18070026-4_mini.jpg)
class="figure_img" id="Figure4"/>
Download
![](http://www.jos.ac.cn:80//style/web/images/down-img.png)
Larger image
![](http://www.jos.ac.cn:80//style/web/images/down-ppt.png)
PowerPoint slide
Figure4.
(Color online) Transmittance of films fabricated at fixed substrate temperature of 500 °C but RF power ranged from 0 to 300 W.
Fig. 5 shows morphology of samples by AFM. The surface morphology of sample without plasma treatment showed column shaped crystallites. This is a sign of typical island growth. Samples with plasma treatment also showed column shaped crystallites. The columns in AFM image of samples with plasma treatment are finer, denser, and trenches in between columns are shallower as applied RF power increases. it is also shown in Fig. 6 that the root mean squared (RMS) roughness of samples with higher RF power treatment is much lower than the samples with lower RF power plasma treatment or no treatment. In addition, the RMS roughness for samples with plasma treatment appears to decrease linearly with respect to the RF power applied.
![](http://www.jos.ac.cn/fileBDTXB/journal/article/jos/2019/12/PIC/18070026-5_mini.jpg)
class="figure_img" id="Figure5"/>
Download
![](http://www.jos.ac.cn:80//style/web/images/down-img.png)
Larger image
![](http://www.jos.ac.cn:80//style/web/images/down-ppt.png)
PowerPoint slide
Figure5.
(Color online) Surface morphology of Ga2O3 film at 0.01 Pa and at (a) 500 °C, 0 W; (b) 500 °C, 100 W; (c) 500 °C, 200 W; (d) 500 °C, 300 W on a 10 × 10 μm2 area.
![](http://www.jos.ac.cn/fileBDTXB/journal/article/jos/2019/12/PIC/18070026-6_mini.jpg)
class="figure_img" id="Figure6"/>
Download
![](http://www.jos.ac.cn:80//style/web/images/down-img.png)
Larger image
![](http://www.jos.ac.cn:80//style/web/images/down-ppt.png)
PowerPoint slide
Figure6.
Dependence of root-mean-squared surface roughness of Ga2O3 film on RF power ranged from 0 to 300 W at fixed substrate temperature of 500 °C.
As shown from the above results, plasma treated samples show a significant increase of heteroepitaxial growth without losing crystallinity compared to a film without plasma treatment. One possible explanation is that crystallization growth of β-Ga2O3 follows the metal-insulator transition mechanism as proposed by Nagarajan et al.[26]. During crystallization, nucleation site starts to form. As the nucleation site expands, it uses more oxygen and leaves gallium atoms in higher concentration in the amorphous region. In other word, the process of β-Ga2O3 crystallization “pushes” the gallium atom concentration higher in the amorphous region.
When plasma treatment was not applied, the deficiency of oxygen atom near the surface makes it much more likely to form the gaseous, volatile gallium suboxide, such as Ga2O. This process was repeatedly reported in several studies of Ga2O3 growth in MBE process[27, 28]. When plasma treatment was applied, oxygen radicals migrated deep into the film and mitigated the formation of gallium concentration near the film surface. Zhen et al.[29] used an oxygen isotopic tracer to show that the concentration of background monoatomic oxygen in SnO2 film deposited by plasma-assisted PLD method was at least 50%, whereas concentration of background diatomic oxygen in SnO2 film deposited in non-reactive background was only 1%–4%. Ambient oxygen atom migrated much deeper into the film in reactive case than it was in non-reactive case. The same group found similar result for ZnO using PLD[30]. In addition, it is speculated that the growth rate of the plasma treated film did not increase as the applied RF power increased because the oxygen partial pressure and the amount of available monatomic oxygen remains the same as RF power increases. Since the plasma source cannot maintain capacitive discharge at 0.01 Pa if RF power dropped below 100 W, therefore is impossible to see if growth rate will gradually increase as RF power increase from 0 to 100 W.
The AFM images in Fig. 5 and roughness of surface relationship with applied RF power in Fig. 6 showed some insight of the effect of increased RF power. It is speculated that higher RF power results in more nucleation sites. As shown in Fig. 5, the crystallites are tall and big in the film grown without plasma treatment because the nucleation sites are scattered sparsely. Therefore, there is enough space for the crystallites to grow large and tall. However, as the RF power increase, the density of crystallites columns increases. This indicates that as RF power increases, more nucleation sites are available. The same amount of arriving species had to be shared by more nucleation sites. As a result, each crystallite is small and short and the roughness of sample at higher RF power showed smaller surface roughness.
4.
Conclusion
Monoclinic β-Ga2O3 films were fabricated by oxygen plasma-assisted PLD method. A film grown in oxygen radical ambient is 2.7 times thicker than films grown in non-reactive O2 background. Increasing strength of RF power showed small increase on growth rate of monoclinic β-Ga2O3 film. XRD and Raman spectroscopy verified that β-Ga2O3 films grown in oxygen radical ambient at 500 °C. The film also showed typical island growth and film grown at higher RF power showed a smoother surface than film grown at lower RF power or no plasma. Transmittance of these films is at least 80% and shows sharp absorption edge at 250 nm. It is speculated that a higher film growth rate in the reactive case is because monoatomic oxygen can migrate deep into the as-deposited film to support Ga2O3 formation and ease the excess concentration of Ga atom near the surface so that Ga2O formation is mitigated. Further research by manipulating oxygen pressure and laser pulse setting should change the crystalline quality and growth rate. In addition, using an oxygen isotopic tracer to study the concentration of background oxygen atom in Ga2O3 would help to reveal the the mechanisms of Ga2O3 heteroepitaxial growth.
Acknowledgements
This work was partially supported by the Scientific Research (No. 16K06268) and the Partnership Project for Fundamental Technology Researches of the Ministry of Education, Culture, Sports, Science and Technology, Japan.