The monocrystalline Si thin film peeled off using adhesive tape. Credit:CrystEngComm
A research team from Tokyo Institute of Technology (Tokyo Tech) and Waseda University have successfully produced high-quality thin film monocrystalline silicon with a reduced crystal defect density down to the silicon wafer level at a growth rate that is more than 10 times higher than before. In principle, this method can improve the raw material yield to nearly 100 percent. Therefore, it can be expected that this technology will make it possible to drastically reduce manufacturing costs while maintaining the power generation efficiency of monocrystalline silicon solar cells, which are used in most high efficient solar cells.
Efficiently converting solar energy to generate electricity is an effective solution to the problem of global warming related to CO2emissions. By making the monocrystalline Si solar cells that are at the core of solar power generation systems thinner, it is possible to greatly reduce raw material costs, which account for about 40 percent of the cost of current modules. Making them flexible and lighter would increase usage and decrease costs.
In addition, as a method of reducing manufacturing cost, thin-film monocrystalline Si solar cells that use a doubleporous siliconlayer (DPSL) via lift-off are attracting attention. Among the technical challenges related to monocrystalline Si solar cells using lift-off are (1) the formation of a high-quality thin film Si at the Si wafer level, (2) achieving a porous structure that can easily be lifted off (peeled off), (3) improving thegrowth rateand Si raw material yield (necessary equipment costs are determined by the growth rate), and (4) being able to use the substrate after lift-off without any waste.
In order to overcome challenge (1), it was necessary to clarify the main factors that determine the quality of thin film crystals grown on poroussilicon, and to develop a technique for controlling these.
A joint research team consisting of Professor Manabu Ihara and Assistant Professor Kei Hasegawa of the Tokyo Tech, and Professor Suguru Noda of Waseda University has developed a high-quality thin film monocrystalline silicon with a thickness of about 10 μm and a reduced crystal defect density down to the silicon wafer level at a growth rate that is more than 10 times higher than before. First, double-layer nano-order porous silicon is generated on the surface of a monocrystalline wafer using an electrochemical technique. Next, the surface was smoothed to a roughness of 0.2 to 0.3 nm via a unique zone heating recrystallization method (ZHR method), and this substrate was used for high-speed growth to obtain a monocrystalline thin film with high crystal quality. The grown film can be easily peeled off using the double-layer porous Si layer, and the substrate can be reused or used as an evaporation source for thin film growth, which greatly reduces material loss. When the surface roughness of the underlying substrate is reduced by changing the ZHR method conditions, the defect density of the thin film crystal that was grown decreased, and the team eventually succeeded in reducing it to the Si wafer level of about 1/10th. This quantitatively shows that a surface roughness in the range of only 0.1-0.2 nm (level of atoms to several tens of layers) has an important impact on the formation of crystal defects, which is also of interest as a crystal growth mechanism.
The film formation rate and the conversion rate of the Si source to the thin film Si are bottlenecks in the production of thin-film monocrystalline Si. With chemical vapor deposition (CVD), which is mainly used for epitaxy, the maximum film forming rate is a few μm/h and the yield is about 10 percent. At the Noda Laboratory of Waseda University, instead of the regular physical vapor deposition (PVD) where raw Si is vaporized at around its melting point of 1414 ?C, by vaporizing the raw Si at much higher temperature of >2000 degrees C, a rapid evaporation method (RVD) was developed with a high Si vapor pressure capable of depositing Si at 10 μm/min. The researchers found that the ZHR technology resolves technical problems and drastically reduces the manufacturing cost of the lift-off process.
Based on the results of this study, not only did the team discover the main factors for improving the quality of crystals during rapid growth on porous silicon used for the lift-off process, they succeeded in controlling them. The results are published in the Royal Society of Chemistry (RSC) journalCrystEngCommand will be featured on the inside front cover of the issue.
Explore further:Imec reports record efficiencies for large-area epitaxial thin-film silicon solar cells
More information:Kei Hasegawa et al, Critical effect of nanometer-size surface roughness of a porous Si seed layer on the defect density of epitaxial Si films for solar cells by rapid vapor deposition,CrystEngComm(2018).DOI: 10.1039/C7CE02162C
Provided by:Tokyo Institute of Technology