English Abstract
A highly sensitive chemosensor for solution based on organic semiconductor laser gain media
Chi Lang,Fei Hong-Tao,
Wang Teng,
Yi Jian-Peng,
Fang Yue-Ting,
Xia Rui-Dong
1.Key Laboratory for Organic Electronics and Information Displays and Institute of Advanced Materials, Jiangsu National Synergetic Innovation Center for Advanced Materials, Nanjing University of Posts and Telecommunications, Nanjing 210023, China
Fund Project:Project supported by the National Natural Science Foundation of China (Grant Nos. 61376023, 61136003), the Priority Academic Program Development of Jiangsu Higher Education Institutions and the Natural Science Foundation of Nanjing University of Posts and Telecommunications, China (Grant Nos. NY212013, NY213044).Received Date:11 October 2015
Accepted Date:26 November 2015
Published Online:05 March 2016
Abstract:Laser has been widely applied in the scientific and engineering areas including communications, medical treatment, industry, and military due to its extremely strict monochromaticity, high coherence and high energy density. Organic laser based on solution processable polymer gain media has attracted considerable attention in various applications due to its easy fabrication, compact system and flexibility. At present, the chemosensors based on organic semiconductor laser have been widely developed. It has been reported to achieve solution monitoring by organic DFB (distributed feedback) laser. Although the method has its own advantages, there are still many operability and craftsmanship problems to be resolved. In this paper we introduce a new type of the real-time monitoring for various solution. The monitor is realized by using amplified spontaneous emission (ASE) from optically pumped organic semiconductor gain media. The gain media comprising blends of poly(9, 9-dioctylfluorene-co-benzothiadiazole) (F8BT) and poly(3-hexylthiophene) (P3HT) at a ratio of 15:85 wt.% is dissolved into toluene (25 mg/mL). Thin films (90 nm thickness) of P3HT/F8BT are obtained by spin coating (2000 rpm) from solution onto pre-cleaned quartz substrates. The P3HT/F8BT film demonstrates the absorption peak at 471 nm, the PL peak at 622 nm, and the ASE peak at 661 nm with FWHM (full-width-at-half-maximum) linewidth of ～ 10 nm under the stripe laser pumping. The thin films are, then, covered by droplet of solution to form planar waveguide structure with variable effective refractive index. Upon analyte binding, a change in refractive index at the P3HT/F8BT film surface results in a change in the effective refractive index of the planar waveguide and in turn induces shift of the ASE mode wavelength and variation of ASE threshold of the organic gain media. The changes in ASE wavelength and threshold can be monitored for sensing. The red shift of 4.5 nm in the ASE spectrum is from 661 to 665.5 nm and the threshold increases from 0.579 J/pulse to 1.447 J/pulse which can be detected with the concentration of sodium chloride increasing from 0 to 25 wt.% in pure water. Our experimental results show that this method is easy to detect the concentration grads of 1 wt.% sodium chloride solution. The measurement sensitivity of solution reaches 97.8 nm/RIU (refractive index unit), and accuracy reaches 141.9 nm/RIU. Furthermore, we demonstrate that the chemosensor could be used for detecting different kinds of solution in the same concentration. The ASE peak position and threshold display clearly different when the droplet 10 wt.% sodium, chloride solution and hydromel solution onto P3HT/F8BT film. Our study suggests that the organic gain media films have potentiality to be developed as a high sensitivity and high accuracy chemosensor to detect solution due to the high sensitivity of the ASE peak position and threshold to the refractive index of the solution.